Abstract:The picture shows vermiculite modified with silane coupling agent KH570. VMT/PBAT and OVMT/PBAT composite films were prepared by solution method. The structure, thermal properties, crystalline properties, rheological properties, cross‐sectional microstructure, and tensile properties of the pure PBAT films, VMT/PBAT, and OVMT/PBAT composite films were tested and comparatively analyzed. The results showed that the OVMT was uniformly dispersed in the matrix in the composites with the addition of modifiers, the thermal stability of the composite films was relatively improved, the initial decomposition temperature of the OVMT/PBAT composite films was about 2–4°C higher than that of the VMT/PBAT composite films, and the complex viscosity was also greater with improved viscoelasticity. The mechanical properties of the OVMT/PBAT‐20% composite films were higher than those of the VMT/PBAT composite films. The mechanical properties of the OVMT/PBAT‐20% films were 35.9% higher in tensile strength and 10.8% higher in elongation at break than the VMT/PBAT‐20% films. Vermiculite (VMT) was used as a filler and it was modified with silane coupling agent KH570 to produce OVMT. VMT/PBAT and OVMT/PBAT composite films were prepared using the solution method using polybutylene terephthalate (PBAT) as a matrix. The structure, thermal properties, crystalline properties, rheological properties, cross‐sectional microstructure, and tensile properties and antibacterial properties of the pure PBAT film, VMT/PBAT, and OVMT/PBAT composite films were tested, including comparative analysis. The results showed that VMT was successfully modified with silane coupling agent to produce OVMT. Furthermore, the thermal stability of VMT/PBAT and OVMT/PBAT composite films decreased compared with pure PBAT film. As the content of VMT and OVMT increases, the energy storage modulus and loss modulus of VMT/PBAT and OVMT/PBAT composite films increase, while the loss factor, complex viscosity and crystallinity gradually decrease. Additionally, the tensile strength and elongation at break of VMT/PBAT and OVMT/PBAT composite films decrease. All three films had no effect on Staphylococcus aureus or Escherichia coli. The modification of VMT with the silane coupling agent KH570 improved the compatibility of OVMT with PBAT, resulting in improved mechanical properties of the OVMT/PBAT composite film compared with the VMT/PBAT composite film. The mechanical properties of the OVMT/PBAT‐20% composite film increased by 35.9% in tensile strength and 10.8% in elongation at break compared with the VMT/PBAT‐20% composite film. Highlights VMT successfully modified with silane coupling agent to produce OVMT. The modification promotes the compatibility of the filler with PBAT. VMT modification helps to improve the mechanical properties of composite materials. Vermiculite modification helps to improve the toughness of composite materials.

Structure and Properties of Organic-Vermiculite/Polyimide Composite Films

In-situ Synthesis, Thermal and Mechanical Properties of Biobased Poly(ethylene 2,5-Furandicarboxylate)/montmorillonite (PEF/MMT) Nanocomposites

Preparation and imidization of polyimide composites filled with boron nitride

PREPARATION AND STUDY ON STRUCTURE OF THE POLYIMIDE/SILICA HYBRID AND NANOCOMPOSITE FILMS

The Morphology and Mechanical Properties of the Hybrid Films of Styrene-Butyl Acrylate Block Copolymer/Mmt from Colloid Blending

Preparation and Structure of Polystyrene/Montmorillonite Nanocomposite

Preparation and properties of silane coupling agent modified vermiculite and its composite films

Thermally Stable and Mechanically Strong Mesoporous Films of Poly(ether Imide)-Based Triblock Copolymers

Structure Characteristics and Thermal Properties of Silane-Grafted-Polyethylene/Clay Nanocomposite Prepared by Reactive Extrusion

Preparation and Characterization of Anisotropic Chain Structures in Polyimide Films

Microstructure and Properties of Organosoluble Polyimide/silica Hybrid Films

Fabrication and Properties of Thermosensitive Organic/inorganic Hybrid Hydrogel Thin Films.

Polyimide/mica hybrid films with low coefficient of thermal expansion and low dielectric constant

Preparation and characterization of poly(propylene carbonate)/montmorillonite nanocomposites by solution intercalation

Polyhedral oligosilsesquioxane-modified boron nitride enhances the mechanical properties of polyimide nanocomposites

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Comparison of Hybrid Polyimide Films with Silica and Organosilica Obtained Via Sol–gel Process

Preparation and Characterization of a Novel Organophilic Vermiculite/poly(methyl Methacrylate)/1-Butyl-3-methylimidazolium Hexafluorophosphate Composite Gel Polymer Electrolyte

Polyimide/montmorillonite nanocomposites based on thermally stable, rigid-rod aromatic amine modifiers

Structure stability of organic montmorillonite used for preparing polyethylene/montmorillonite nanocomposite

Preparation and properties of triphenyl octylphosphonium bromide‐modified vermiculite and its PBAT composite films