Abstract:The size effect in the fracture of solids represents a highly critical issue with a prolonged history of research. The size effect of traditional quasi-brittle materials can already be well described through the size effect model. However, there is still a lack of research on the size effect of strain-hardening cementitious composites (SHCC), a special type of fibre-reinforced concrete with macro-scale strain-hardening behaviour after first cracking. Being distinct from traditional quasi-brittle materials with softening nature, SHCC is thus expected to behave differently in terms of size effect. In this research, the structural size effect problem of SHCC is comprehensively studied by experimental investigation and theoretical analysis. Geometrically similar notched three-point bending specimens were tested in mode I and mixed mode I/II fracture condition. The whole-process of failure and matrix cracking zone around the main crack was captured with high resolution by digital image correlation technology. Experimental results showed that apparent fracture energy, nominal strength, structural ductility and fracture resistance curve are all structural size-dependent. The apparent fracture energy was shown to arise with specimen size within the tested range. This is related to large-scale pseudo yielding, i.e. enlargement of matrix cracking zone (like the yielding zone in metals) with increasing structural size. It thus provides an indirect method for the estimation of cohesive fracture energy of single crack with constitutive nature. Due to the scaled matrix cracking zone, an intermediate asymptote exists in the size effect curve of nominal strength, in addition to the plastic and LEFM asymptotes in the Bažant original size effect law. This resembles the recent finding of intermediate asymptote in plastic-hardening metal( Dönmez et al. 2023 ). The size-dependence of R-curve was also examined. Though size-dependent, the equivalent LEFM-based R-curves are shown to have three common stages reflecting different cracking processes. Based on experimental results, the size effect of fracture energy and nominal strength are finally modelled theoretically in the Bažant's framework of equivalence between energy release and fracture resistance.

Tests and numerical simulation of size effect on the strength of self-compacting concrete

Mesoscopic numerical test of crushing process of concrete under uniaxial compression

Effect of Aggregate on Cracking Behaviours of Concrete in Mesoscopic Modeling

Experimental Research on Large-scale Square Columns Confined with Wrapped CFRP under Axial Compressive Load

Experimental investigation on the effect of coarse aggregate size and silica fume dosage to the fracture parameters of concrete

Numerical and theoretical investigation on the size effect of concrete compressive strength considering the maximum aggregate size

Experimental Study on the Size Effect on the Probability Distribution of Concrete Compressive Strength

An Experimental Study of Dynamic Compression Performance of Self-Compacting Concrete

Study on the Material Mechanical Performance of Large Scale Self-Compacting Rock-Filled Concrete

Size Effect On The Cubic Compressive Strength Of Reactive Powder Concrete

Size effect on compressive strength of foamed concrete: Experimental and numerical studies

Experimental Study and Failure Criterion Analysis on Combined Compression-Shear Performance of Self-Compacting Concrete

Numerical analysis of concrete strength size effect on meso-level

Numerical Experiment on Size Effect for Sfrc Splitting Fracture

Size effect of square concrete-filled steel tubular columns subjected to lateral shear and axial compression: Modelling and formulation

Experimental study on fracture properties of self-compacting concrete

Numerical investigation of the failure mechanism of cubic concrete specimens in SHPB tests

Size effect of axially-loaded CFRP ring-confined circular concrete columns: 3D mesoscale simulation

Investigation on size effects of ultra-high-performance concrete: experimental and numerical study

Structural size effect in the mode I and mixed mode I/II fracture of strain-hardening cementitious composites (SHCC)

Monte Carlo Simulations of Mesoscale Fracture of Concrete with Random Aggregates and Pores: A Size Effect Study