Abstract:To investigate mechanical behavior on in & post impact of CFRP tubes varying wall thickness and impactor, low‐velocity impact (LVI), compression‐after‐impact (CAI), and flexure‐after‐impact (FAI) tests were conducted and three main conclusions can be obtained. First, because of the point‐line contact for flat impactor, two peaks are found in the force‐displacement curves. Second, the failure mode of CAI is brittle fracture at the impact circumferential area. Third, FAI strength mainly depends on the no‐impact surface of tubes. With the help of the high‐speed camera and self‐designed fixture, it was investigated that the effects of the impactors in a variety of shapes on the mechanical behavior and failure mode of carbon fiber‐reinforced polymer (CFRP) tubes with a range of inner diameter during the low‐velocity impact (LVI) of four impact energies. Then, the three‐dimensional digital image correlation (3D‐DIC) system was carried out to monitor the damage evolution of the LVI‐damaged specimens under compressive and flexural loading. In addition, the residual compressive and flexural strength of all kinds of cases were compared and discussed. The results show that the increase in wall thickness can improve the LVI, compression‐after‐impact (CAI), and flexure‐after‐impact performance. The failure mode of compression changes to brittle fracture failure at the impact circumferential region. The CAI strength of the specimen damaged by a flat impactor is 23.89% less than that of a hemispherical one, but there is little difference in flexural loading. Highlights Mechanical behavior on in & post LVI of CFRP tubes varying wall thickness and impactor. Due to point‐line contact for flat impactor, two peak forces are in the F‐D curves. LVI property and residual strength are improved with the increase of wall thickness. Compressive failure mode is brittle fracture at the impact circumferential area. Flexure‐after‐impact strength mainly depends on the no‐impact surface of tubes.

Investigation on Mechanical Behavior of Filament-Wound Cfrp Tubes

Modelling of Concrete-Filled Filament-Wound FRP Confining Tubes Considering Nonlinear Biaxial Tube Behavior

Characteristic Investigation on Strength of Filament-Wound CFRP Tubes

Experimental and numerical study of mechanical properties of filament-wound CFRP tubes

CHARACTERISTIC ANALYSIS AND EXPERIMENTAL INVESTIGATION ON STRENGTH OF FILAMENT-WOUND CFRP TUBES

Study on Behaviors of FRP Confined Stub Concrete Filled Square Steel Tubes under Axial Load

Quasi-static Axial Crushing and Transverse Bending of Double Hat Shaped CFRP Tubes

Experimental Study on Axial Compressive Behavior of Concrete-Filled FRP Filament-winded Tubes

Experimental and Numerical Study on CFRP Tubes under Axial Crushing

Behavior of CFRP-strengthened Short Spiral Welded Tubes under Axial Load

Behavior Analysis of FRP Tube/filling Strengthened Steel Members under Axial Compression

Experimental Research on Concrete-Filled GFRP Tubes and GFRP-Steel Composite Tubes under Axial Compressive Load

On crushing responses of filament winding CFRP/aluminum and GFRP/CFRP/aluminum hybrid structures

Experimental and numerical simulation on axial compression of GFRP-long-tube under quasi-static and dynamic loads

Experimental investigation into dynamic axial impact responses of double hat shaped CFRP tubes

Behavior of Concrete-Filled Frp Tubes under Cyclic Axial Compression

Experimental investigation on the low‐velocity impact response and the residual strength of CFRP tubes

Analysis-oriented Model for FRP Tube-Confined Concrete: 3D Interpretation of Biaxial Tube Behaviour

Behavior and Modeling of Ultra-High Performance Concrete-Filled FRP Tubes under Cyclic Axial Compression

Investigation on Failure Behavior of Carbon Fiber Reinforced Polymer Wire Subjected to Combined Tension and Bending

Investigation and Calculation Method for the Mechanical Properties of Filament Wound Profiles for Deformed Shield Tunnel Reinforcement