Abstract:A critical issue to tackle before successful commercialization of solid oxide fuel cells (SOFCs) can be achieved is the long-term thermal stability required for SOFCs to operate reliably without significant performance degradation despite enduring thermal cycling. In this work, the impact of thermal cycling on the durability of NiO-yttria-stabilized zirconia-based anode-supported cells is studied using three different heating/cooling rates (1, 2, and 5 °C min-1) as the temperature fluctuated between 400 and 700 °C. Our experiments simulate time periods when power from SOFCs is not required (e.g., as might occur at night or during an emergency shutdown). The decay ratios of the cell voltages are 8.8% (82 μV h-1) and 19.1% (187 μV h-1) after thermal cycling testing at heating/cooling rates of 1 and 5 °C min-1, respectively, over a period of 1000 h. The results indicate SOFCs that undergo rapid thermal cycling experience much greater performance degradation than cells that experience slow heating/cooling rates. The changes in total resistance for thermally cycled cells are determined by measuring the Rpol of the electrodes (whereas the ohmic resistances of the cells remain unchanged from their initial value), signifying that electrode deterioration is the main degradation mechanism for SOFCs under thermal cycling. In particular, fast thermal cycling leads to severe degradation in the anode part of SOFCs with substantial agglomeration and depletion of Ni particles seen in our characterizations with field emission-scanning electron microscopy and electron probe microanalysis. In addition, the mean particle size in the cathode after thermal cycling testing increases from 0.104 to 0.201 μm for the 5 °C min-1 cell. Further, the presence of Sr-enriched regions is more significant in the La0.6Sr0.4Co0.2Fe0.8O3-δ cathode after fast thermally cycled SOFCs.

Quantitative Analysis of Micro Structural and Conductivity Evolution of Ni-YSZ Anodes During Thermal Cycling Based on Nano-Computed Tomography

Analysis of Three-Dimensional Microstructure Evolution of Tested Ni-YSZ Anodes by Nano-CT

Modeling of Gas Transport with Electrochemical Reaction in Nickel-Yttria-Stabilized Zirconia Anode During Thermal Cycling by Lattice Boltzmann Method

Degradation Mechanisms of Solid Oxide Fuel Cells under Various Thermal Cycling Conditions

Quantitative analysis methods for three-dimensional microstructure of the solid-oxide fuel cell anode

Microstructural Degradation of Ni/YSZ Electrodes in Solid Oxide Electrolysis Cells under High Current

Lattice-Boltzmann modeling of gas transport in Ni-Yttria-stabilized zirconia anodes during thermal cycling based on X-ray computed tomography

Failure Analysis of Ni-8YSZ Electrode under Reoxidation Based on the Real Microstructure

Analysis of the Three-Dimensional Microstructure of a Solid-Oxide Fuel Cell Anode Using Nano X-ray Tomography

Tracking solid oxide cell electrode microstructural evolution during annealing by scanning 3D X-ray diffraction microscopy

Impact of yttria-stabilized zirconia contents in nickel cermet anodes for intermediate temperature-operated syngas-fueled thin film solid oxide fuel cells

Microstructure Evolution Analysis of Ni/YSZ Cermet Electrode using Cross-Sectional Model Cells

Degradation of Ni-YSZ Electrodes in Solid Oxide Cells: Impact of Polarization and Initial Microstructure on the Ni Evolution

Evaluation of Carbon Deposition Behavior on the Nickel/yttrium-Stabilized Zirconia Anode-Supported Fuel Cell Fueled with Simulated Syngas

Quantitative study on solid oxide fuel cell anode microstructure stability based on 3D microstructure reconstructions

Effects of operating conditions on the performance degradation and anode microstructure evolution of anode-supported solid oxide fuel cells

Electrochemical and Microstructural Characterization of Cyclic Redox Behaviour of SOFC Anodes

Fracture Simulation of Ni-YSZ Anode Microstructures of Solid Oxide Fuel Cells Using Phase Field Method

The Detection of Monoclinic Zirconia and Non-Uniform 3D Crystallographic Strain in a Re-Oxidized Ni-YSZ Solid Oxide Fuel Cell Anode

Effects of Initial Reduction Temperature on the Microstructures and Performances of Ni/YSZ Anodes for Solid Oxide Fuel Cells

Microstructure Tailoring of the Nickel Oxide-Yttria-Stabilized Zirconia Hollow Fibers Toward High-Performance Microtubular Solid Oxide Fuel Cells