Abstract:Nickel/yttria-stabilized zirconia (YSZ) composites are the most commonly used fuel electrodes for solid oxide cells. While microstructural changes of Ni/YSZ during operational conditions have been thoroughly investigated, there is limited knowledge regarding Ni/YSZ surface chemistry under working conditions. In this study, we examine the interaction between Ni/YSZ electrodes and water vapor under open circuit and polarization conditions, utilizing near ambient pressure soft and hard X-ray photoelectron spectroscopies. Miniature cells with conventional porous Ni/YSZ composite cermet cathodes were modified to facilitate the direct spectroscopic observation of the functional electrode's areas close to the interface with the YSZ electrolyte. The results highlight dynamic changes in the oxidation state and composition of Ni/YSZ under H2 and H2O atmospheres. We also quantify the accumulation of impurities on the electrode surface. Through adjustments in the pretreatment of the cell, the correlation between the nickel surface oxidation state and the cell's electrochemical performance during H2O electroreduction is established. It is unequivocally shown that nickel surface oxidation in H2O electrolysis favors NiO over Ni(OH)x, providing critical insights into the mechanism of Ni-phase redistribution within the electrode during long-term operation. Depth-dependent photoemission measurements, combined with theoretical quantitative simulations, reveal that NiO and Ni phases are uniformly mixed on the surface during H2O electrolysis. This differs from the conventional expectation of a NiO-shell/Ni-core configuration in gas phase oxidation. These findings provide crucial insights into the surface chemistry of Ni/YSZ electrodes under conditions relevant to H2O electrolysis, elucidating their impact on the electrochemical performance of the cell.

Microstructure Evolution Analysis of Ni/YSZ Cermet Electrode using Cross-Sectional Model Cells

Degradation of Ni-YSZ Electrodes in Solid Oxide Cells: Impact of Polarization and Initial Microstructure on the Ni Evolution

Ni migration of Ni-YSZ electrode in solid oxide electrolysis cell: An integrated model study

Time-Dependence of Microstructural Evolution and Performance Degradation of Ni/YSZ Electrode in Co-Electrolysis SOEC

Modeling Microstructure Evolution of Ni Cermet Using a Cellular Automaton Approach

Impact of yttria-stabilized zirconia contents in nickel cermet anodes for intermediate temperature-operated syngas-fueled thin film solid oxide fuel cells

Failure Analysis of Ni-8YSZ Electrode under Reoxidation Based on the Real Microstructure

Role of Initial Microstructure on Nickel-Ysz Cathode Degradation in Solid Oxide Electrolysis Cells

Understanding Degradation Behavior of Direct-Ammonia Solid Oxide Fuel Cells Using Nanoscale Analyses

Hierarchical dual-porosity nanoscale nickel cermet electrode with high performance and stability

Review of factors affecting the performance degradation of Ni-YSZ fuel electrodes in solid oxide electrolyzer cells

A Model of Solid Oxide Fuel Cell Degradation on a Microstructural Level

Unveiling Key Interface Characteristics of Ni/Yttria-Stabilized Zirconia Solid Oxide Cell Electrodes in H2O Electroreduction Using Operando X-ray Photoelectron Spectroscopy

Integrated 3D Modeling Unravels the Measures to Mitigate Nickel Migration in Solid Oxide Fuel/Electrolysis Cells

Carbon Deposition on Patterned Nickel/yttria Stabilized Zirconia Electrodes for Solid Oxide Fuel Cell/solid Oxide Electrolysis Cell Modes

Tailoring the Microstructure of a Solid Oxide Fuel Cell Anode Support by Calcination and Milling of YSZ

Effects of operating conditions on the performance degradation and anode microstructure evolution of anode-supported solid oxide fuel cells

Ni / GDC Fuel Electrode for Low-Temperature SOFC and its Aging Behavior Under Accelerated Stress

Modeling Of An Anode-Supported Ni-Ysz Vertical Bar Ni-Scsz Vertical Bar Scsz Vertical Bar Lsm-Scsz Multiple Layers Sofc Cell - Part Ii. Simulations And Discussion

Simulation of Eis Spectra and Polarization Curves Based on Ni/Ysz Patterned Anode Elementary Reaction Models

Studying the Sulfur Poisoning Mechanism of Solid Oxide Fuel Cells by Means of Patterned Nickel/Yttrium-Stabilized Zirconia Electrodes