Microstructure and Magnetic Behaviors of FeSi-ZrO2 Nanocomposite Films

Youran Yang,Li Zhong,Weihua Lan,Xiaofang Bi

DOI: https://doi.org/10.1007/s12598-011-0341-2

2011-01-01

Abstract:FeSi-34 wt.% ZrO 2 nanocomposite films were prepared by EB-PVD technique to investigate the effect of a two-phase microstructure on magnetic behaviors. X-ray diffraction analysis and TEM observations reveal that the as-deposited film is composed of Fe(Si) nanocrystallites and amorphous-like FeSi-ZrO 2 phase. Isothermal annealing leads to further crystallization of Fe(Si) from the FeSi-ZrO 2 phase, which results in the increase in magnetization of the film. Owing to the increase of magnetization and the relief of stress, coercivity is reduced at the initial stage of the annealing. However, the variation of coercivity with grain size deviates from the D 6 rule, which, instead, follows a D 3/2 relationship. The result was discussed by taking into account the two-phase microstructure characterized by magnetic particles coexisted with non-magnetic phase.