Abstract:Millimeter-sized ZTA (zirconia toughened alumina) particles + WC (tungsten carbide) particles reinforced hypereutectic high chromium cast iron (H-HCCI) composites were prepared by liquid phase sintering. The volume fraction, stacking method and sintering process of the reinforced particles in the composites were designed. The interfacial bonding mechanism between the reinforcements and the matrix in the composites was systematically discussed. The results show that when the sintering temperature is 1380 °C, the volume percentage of ZTA particles, WC particles and H-HCCI is set to 10, 30 and 60%, respectively, and the reinforced particles are mixed and stacked, the prepared sample has the best performance. The average nano-hardness of ZTA particles, the interface layer between ZTA particles and H-HCCI matrix, WC particles and H-HCCI matrix in the composites are 20.83, 19.08, 23.33 and 16.39 GPa, respectively. The Young's moduli of each component in the composites are 330.56, 289.41, 300.68 and 232.11 GPa, respectively. Based on the results of friction and wear experiments, the average wear depth of ZTA particles is 6.589 μm, the average wear depth of WC particles is 4.872 μm, and the average wear depth of H-HCCI matrix is 9.802 μm.Through performance testing, it was found that the hybrid reinforced composites showed excellent comprehensive properties. This paper provides theoretical support for multiphase reinforced composites, and proposes a new method for preparing ZTA particle reinforced metal matrix composites, which realizes the metallurgical interface bonding between ceramics and metals.

Preparation of ZrO 2-Al 2O 3 honeycomb ceramic reinforced high Cr cast iron matrix composites by composite processing

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Fabrication of Composites with Honeycomb-Shaped Ceramic Plates

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites

On the Preparation and Wear Properties of Ceramic Particle-reinforced High-chromium Cast Iron-based Surface Composite Material

Effect of quenched-tempered heat treatment on the wear resistance mechanism of zirconia toughened alumina ceramic reinforced high chromium cast iron architecture composite

Effect of Interface Wetting Agents on Impact Toughness and Bending Properties of ZrO2-Toughened Al2O3 Particle-Reinforced High Chromium Cast Iron Matrix Composite

Fabrication of ZTA/High Chromium Cast Iron Matrix Composites and Its Abrasive Wear Resistant

Preparation and Properties of ZrO2-5CrMnMo Composites by Ceramic Injection Molding

Three-body Abrasive Wear Resistance of Iron Matrix Composites Reinforced with Ceramic Particles

Preparation and Interface Investigation of Fe/Al2o3p Composite Activated by Ni and Ti

Wearing and interfacial characterization of zirconia toughened alumina reinforced high chromium cast iron composites in an actual working condition

Preparation and Mechanical Properties of Fine Grain Al2O3-ZrO2 Composite Ceramics

Preparation and Characterization of Aluminide/zirconia Composite Coatings by a Three-Step Combined Process

Interfacial characteristics and wear performances of iron matrix composites reinforced with zirconia-toughened alumina ceramic particles

Compression Performance and Abrasive Wear Resistance of CuNi‐Modified Zirconium Oxide‐Toughened Alumina Particles‐Reinforced Iron Matrix Composites

Recent Developments in Fabrication of Ceramic Particle Reinforced Iron Matrix Wear Resistant Surface Composite Using Infiltration Casting Technology

Study on Squeeze Casting Metal-zirconium Composite Die Material by Hot Press Sintering

Preparation of Nano-Composite ZTM Ceramics of High Mechanical Properties by In-Situ Crystallization of Amorphous Bodies

Research Progress on Preparation and Properties of Zirconium Carbide Matrix Composites

ZrO 2 Strengthened NiAl/Cr（Mo,Hf） Composite Fabricated by Powder Metallurgy