Abstract:Millimeter-sized ZTA (zirconia toughened alumina) particles + WC (tungsten carbide) particles reinforced hypereutectic high chromium cast iron (H-HCCI) composites were prepared by liquid phase sintering. The volume fraction, stacking method and sintering process of the reinforced particles in the composites were designed. The interfacial bonding mechanism between the reinforcements and the matrix in the composites was systematically discussed. The results show that when the sintering temperature is 1380 °C, the volume percentage of ZTA particles, WC particles and H-HCCI is set to 10, 30 and 60%, respectively, and the reinforced particles are mixed and stacked, the prepared sample has the best performance. The average nano-hardness of ZTA particles, the interface layer between ZTA particles and H-HCCI matrix, WC particles and H-HCCI matrix in the composites are 20.83, 19.08, 23.33 and 16.39 GPa, respectively. The Young's moduli of each component in the composites are 330.56, 289.41, 300.68 and 232.11 GPa, respectively. Based on the results of friction and wear experiments, the average wear depth of ZTA particles is 6.589 μm, the average wear depth of WC particles is 4.872 μm, and the average wear depth of H-HCCI matrix is 9.802 μm.Through performance testing, it was found that the hybrid reinforced composites showed excellent comprehensive properties. This paper provides theoretical support for multiphase reinforced composites, and proposes a new method for preparing ZTA particle reinforced metal matrix composites, which realizes the metallurgical interface bonding between ceramics and metals.

Fabrication of ZTA/High Chromium Cast Iron Matrix Composites and Its Abrasive Wear Resistant

Three-body Abrasive Wear Resistance of Iron Matrix Composites Reinforced with Ceramic Particles

On the Preparation and Wear Properties of Ceramic Particle-reinforced High-chromium Cast Iron-based Surface Composite Material

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites

Interfacial Bonding and Abrasive Wear Behaviours of the Iron Matrix Composites

The Fabrication and Properties of Particle Reinforced Cast Metal Matrix Composites

Recent Developments in Fabrication of Ceramic Particle Reinforced Iron Matrix Wear Resistant Surface Composite Using Infiltration Casting Technology

Microstructure and wear characteristics of ATZ ceramic particle reinforced gray iron matrix surface composites

Interfacial characteristics and wear performances of iron matrix composites reinforced with zirconia-toughened alumina ceramic particles

Elucidation of Abrasive Wear and Slurry Erosion Behavior of Fe Matrix Composites Reinforced with Metallic Coating Modified ZTAP Ceramics

Effect of quenched-tempered heat treatment on the wear resistance mechanism of zirconia toughened alumina ceramic reinforced high chromium cast iron architecture composite

Wearing and interfacial characterization of zirconia toughened alumina reinforced high chromium cast iron composites in an actual working condition

Achieving the Superior Abrasive Wear Resistance in ZTAP/Fe Composites from the Theoretical Calculations Guided Designing of Metallurgical Interface Transition Layer

Impact-abrasive wear property of ZrO2 toughened Al2O3 ceramic particles reinforced high manganese steel matrix composites

Interfacial characterization and erosive wear performance of zirconia toughened alumina ceramics particles reinforced high chromium white cast irons composites

Compression Performance and Abrasive Wear Resistance of CuNi‐Modified Zirconium Oxide‐Toughened Alumina Particles‐Reinforced Iron Matrix Composites

Three-Body Abrasive Wear Behavior of Iron Matrix Composite Reinforced with Cemented Carbide Particles

Interface and wear characteristics of high-Cr cast iron matrix composite reinforced with cemented carbide particles

MECHANICAL AND WEAR PROPERTIES OF ZTA CERAMICS

Preparation of ZrO 2-Al 2O 3 honeycomb ceramic reinforced high Cr cast iron matrix composites by composite processing