Abstract:We report magnetism of tetragonal β-Fe3Se4 nanoplates controllably synthesized by thermal decomposition at 603 K of inorganic–organic (β-Fe2Se3)4[Fe(tepa)] hybrid nanoplates (tepa = tetraethylenepentamine). (β-Fe2Se3)4[Fe(tepa)] hybrid precursor and β-Fe3Se4 nanoplates are in single crystal features as characterized by selected area electron diffraction. Rietveld refinements reveal that ordered inorganic–organic (β-Fe2Se3)4[Fe(tepa)] hybrid nanoplates are in a tetragonal layered crystal structure with a space group of I4cm (108) and room-temperature lattice parameters are a = 8.642(0) Å and c = 19.40(3) Å, while the as-synthetic tetragonal β-Fe3Se4 nanoplates have a layered crystal structure with the P4/nmm space group, and room-temperature lattice parameters are a = 3.775(8) Å and c = 5.514(5) Å. Magnetic measurements show the weak ferrimagnetism for (β-Fe2Se3)4[Fe(tepa)] hybrid nanoplates at room temperature, while the as-synthetic β-Fe3Se4 nanoplates are antiferromagnetic in a temperature range between 120 and 420 K but in a ferrimagnetic feature below ~120 K. The as-synthetic β-Fe3Se4 nanoplates are thermally instable, which are transformed to ferrimagnetic β-Fe3Se4 nanoplates by annealing at 623 K (a little higher than the synthetic temperature). There is an irreversible change from antiferromagnetism of the as-synthetic β-Fe3Se4 phase to the ferrimagnetism of the as-annealed β-Fe3Se4 phase in a temperature between 420 and 470 K. Above 470 K, the tetragonal β-Fe3Se4 phase transforms to monoclinic Fe3Se4 phase with a Curie temperature (TC) of ~330 K. This discovery highlights that crystal structure and magnetism of Fe-Se binary compounds are highly dependent on both their phase compositions and synthesis procedures.

Selective Synthesis of Fe7se8 Polyhedra with Exposed High-Index Facets and Fe7se8 Nanorods by A Solvothermal Process in A Binary Solution and Their Collective Intrinsic Properties

Two-Dimensional Room-Temperature Magnetic Nonstoichiometric Fe7Se8 Nanocrystals: Controllable Synthesis and Magnetic Behavior.

Two-Dimensional Room-Temperature Magnetic Nonstoichiometric Fe 7 Se 8 Nanocrystals: Controllable Synthesis and Magnetic Behavior

Solventothermal synthesis and morphological control of nanocrystalline FeS2

Synthesis of Polyhedral Iron Oxide Nanocrystals Bound by High-Index Facets

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Composition‐Controllable Syntheses and Property Modulations from 2D Ferromagnetic Fe5Se8 to Metallic Fe3Se4 Nanosheets

Monodisperse Cubic Pyrite NiS2 Dodecahedrons and Microspheres Synthesized by a Solvothermal Process in a Mixed Solvent: Thermal Stability and Magnetic Properties

One-Step Synthesis of Cubic Fes2 and Flower-Like Fese2 Particles by A Solvothermal Reduction Process

Controlled Synthesis and Characterization of Znse Nanostructures Via A Solvothermal Approach in A Mixed Solution

Controlled synthesis and excellent magnetism of ferrimagnetic NiFe2Se4 nanostructures

Metal Ions Induce Growth and Magnetism Alternation of Α‐fe2o3 Crystals Bound by High‐Index Facets

Solvothermal Synthesis of Nanocrystalline Fes2

Self-assembly of 1D FeSe2 Chains and Fe(dien)2 Complexes for Ferrimagnetic Inorganic-Organic Hybrid Cuboids

Diethylenetriamine-Assisted Hydrothermal Route to Synthesize Cuboidal Structure of PbSe Crystal

Free-standing 2D Non-Van Der Waals Antiferromagnetic Hexagonal FeSe Semiconductor: Halide-Assisted Chemical Synthesis and Fe2+ Related Magnetic Transitions.

Controllable one-pot synthesis of FeSe2 nanooctahedra embedded microtubes by a sacrificial self-template method

Magnetism of Tetragonal β-Fe3Se4 Nanoplates Controllably Synthesized by Thermal Decomposition of (β-Fe2Se3)4[Fe(tepa)] Hybrid

Superconducting Two-Dimensional FeSe Grown on the Fe-Enriched Interface.

Facile Solvothermal Synthesis of Uniform Iron Selenide Nanoplates

Shape-controlled Synthesis and Magnetic Properties of FePt Nanocubes