Abstract:Magnetic nanoparticles and thin films exhibiting a large magnetic anisotropy energy density (MAE) have attracted enormous attention over the last years due to their potential use in magnetic data storage or sensing applications. FePt alloy nanoparticles and films have a huge MAE in the chemically ordered L10 phase. This ordered phase is typically obtained by annealing the as-prepared chemically disordered fcc FePt nanoparticles at temperatures above 600°C. Besides standard colloidal approaches [1], such fcc FePt nanoparticles can be fabricated by a micellar technique resulting in regular arrays on various substrates [2,3]. This approach offers the advantage that the interparticle distance can be tuned between 20-100 nm. Due to the larger separation particle agglomeration can be avoided during the annealing induced transformation into the L10 phase. Moreover, the particles are magnetostatically decoupled. We investigated the formation of the L10 phase for 2-10 nm FePt particles as a function of the annealing temperature and time on Si/SiOx substrates. Hysteresis loops at T = 15K reveal strongly enhanced coercive field after an annealing step at 700°C for 30 min compared to the as-prepared particles. The effective MAE is found to be 1-2×10 J/m using simple Stoner-Wohlfarth modeling that is a factor of 3-5 smaller than the FePt bulk MAE. In order to correlate the magnetic properties to the structure of the particles we performed transmission electron microscopy (TEM) investigations of FePt particles on both, Si/SiOx and MgO(001) substrates. Basically, the lowered MAE could originate from defective crystal structures, imperfect ordering of Feand Pt-planes (chemical ordering parameter), and/or inhomogeneous segregation of Fe/Pt within the particles. The applied TEM methods included conventional TEM (bright-field, dark-field, electron diffraction), spherical aberration corrected high resolution imaging and scanning TEM (Z-contrast). It was found that most particles contain defects such as stacking faults and multiple twins (Figure 1). Calculated TEM images based on various models of FePt nanoparticles (Figure 2) were generated and compared to experimental images especially to analyze and to determine the chemical ordering parameter of the L10 phase, crystal structure and defects.

Shape-controlled Synthesis and Magnetic Properties of FePt Nanocubes

Synthesis of FePt Nanocubes Using Mo(Co)6 As a Reducing Agent and Their Magnetic Properties

Shape-Controlled Synthesis and Magnetic Properties of Monodisperse Fe3o4 Nanocubes

Synthesis, Structure and Magnetic Property of L1(0)-FePt Nanoparticles

Structural and Magnetic Investigations on FePt Nanoparticles

Synthesis and Magnetic Studies of Core-Shell FePt@Fe3O4 Nanowires and Nanoparticles

Length-Controllable Catalyzing-Synthesis And Length-Corresponding Properties Of Feco/Pt Nanorods

Oriented-assembly of Hollow FePt Nanochains with Tunable Catalytic and Magnetic Properties.

Monodisperse face-centred tetragonal FePt nanoparticles with giant coercivity

Tuning the Shape of Fept Nanoparticles by Applying High Magnetic Field in Wet-Chemical Process

Tuning Crystal Structure and Magnetic Property of Dispersible FePt Intermetallic Nanoparticles

Synthesis and Magnetic Properties of FePt /silica Core-Shell Nanoparticles

Magnetic properties of FePt nanoparticle assemblies embedded in atomic-layer-deposited Al2O3

Synthesis and Characterization of FePt Nanoparticles and FePt Nanoparticle/sio 2 -Matrix Composite Films

Chemical Synthesis and Magnetic Properties of Well-Coupled Fept/Fe Composite Nanotubes

Shape-controlled Synthesis and Their Magnetic Properties of Hexapod-Like, Flake-Like and Chain-Like Carbon-Encapsulated Fe3O4 Core/shell Composites

Preparation and Magnetic Properties of L10–FePt/TiO2 Nanocomposite Thin Films

Langmuir-Blodgett Self-Assembly and Electrochemical Catalytic Property of FePt Magnetic Nano-Monolayer

Synthesis of CoFe2O4 Nanodot Arrays via Diblock Copolymer Template Method

Synthesis and Magnetic Properties of Fe3Pt Nanowire Arrays Fabricated by Electrodeposition