Abstract:Monodisperse magnetic MnZn ferrite nanostructures with various morphologies have been successfully synthesized via high-temperature decomposition of metal acetylacetonate (acac) in the presence of oleic acid (OA) and oleyamine (OAm). In a classical crystal nucleation/growth process, differential stabilization of OA on specific crystal facets may alter relative crystal growth rates, resulting in the formation of zero-dimensional (0-D) spherical, cubical, and starlike nanocrystals (ca. 9, 11, 16 nm), respectively. Furthermore, shortening nucleation duration might bring a deficient nucleation and a rapid increase in monomer concentration, which accelerates the subsequent growth process of nanocrystals, leading to the formation of the starlike nanocrystals with larger size (ca. 1923 nm). They are further oriented to assemble reciprocally, gradually forming initial three-dimensional (3-D) branched nanoclusters (ca. 3040 nm) to minimize the magnetostatic energy, owing to their size-dependent magnetic dipolar interaction. In addition, the surface-defect-induced secondary growth of the branched nanoclusters may considerably improve their uniformity, accompanied by the size increase in the presence of the monomers, resulting in the final multibranched nanoclusters with formation of sharp or obtuse edges (ca. 4550 nm). Our study reveals the transformation of 0-D nanocrystals to 3-D nanoclusters as well as the shape evolution mechanism, which provide a versatile synthetic strategy for shape-controlled nanostructure. The multibranched nanoclusters have the higher magnetization and magnetically induced heating efficiency in an alternating current magnetic field, which can be used as promising heating agents for biomedical application.

Metal Ions Induce Growth and Magnetism Alternation of Α‐fe2o3 Crystals Bound by High‐Index Facets

Nickel Ions Inducing Growth Of High-Index Faceted Alpha-Fe2o3 And Their Facet-Controlled Magnetic Properties

Inside Cover: Metal Ions Induce Growth and Magnetism Alternation of Α‐fe2o3 Crystals Bound by High‐Index Facets (chem. Eur. J. 29/2012)

Nickel ions inducing growth of high-index faceted α-Fe 2O3 and their facet-controlled magnetic properties

Synthesis of Polyhedral Iron Oxide Nanocrystals Bound by High-Index Facets

Controlled Growth And Magnetic Properties Of Alpha-Fe2o3 Nanocrystals: Octahedra, Cuboctahedra And Truncated Cubes

Shape Evolution of “multibranched” Mn–Zn Ferrite Nanostructures with High Performance: A Transformation of Nanocrystals into Nanoclusters

A Cu2+ Ion–f Center Complex View on the Photoluminescence Quenching and Correlating Ferrimagnetism in (cu2+/cu12+)0.044zn0.956o Electrospun Nanobelts

The Structure-Tunable Synthesis and Magnetic Properties of Fe3o4 Nanocrystals

Al3+-controlled Synthesis and Magnetic Property of Α-Fe2o3nanoplates

Synthesis of ZnFe 2 O 4 Nanomagnets by Fe-ion Implantation into ZnO and Post-Annealing

Α-Fe2o3 Nanocrystals: Controllable SSA-Assisted Hydrothermal Synthesis, Growth Mechanism, and Magnetic Properties

ZnFe2O4 Nanocrystals: Synthesis and Magnetic Properties

Controlling Cation Distribution and Morphology in Colloidal Zinc Ferrite Nanocrystals

Structure-Controllable Synthesis Of Multiferroic Yfeo3 Nanopowders And Their Optical And Magnetic Properties

Icosahedral Face-Centered Cubic Fe Nanoparticles: Facile Synthesis and Characterization with Aberration-Corrected TEM

Enhancing magnetostriction in FeAl alloys via crystal growth orientation tuning by a trace amount of Pt doping

Half-Unit-Cell Alpha-Fe2o3 Semiconductor Nanosheets With Intrinsic And Robust Ferromagnetism

Controlled Synthesis of MnxFe1−xO Concave Nanocubes and Highly Branched Cubic Mesocrystals

Superparamagnetic Nanoparticles Formed in Fe-implanted ZnO

Magnetism of Zno Nanoparticles: Dependence on Crystallite Size and Surfactant Coating