Abstract:Colloidal, monodisperse, single -crystalline pyramidal CuInS2 and rectangular AgInS2 nanocrystals were successfully synthesized through a convenient and improved solvothermal process that uses hexadecylamine as a capping reagent. The crystal phase, morphology, crystal lattice, and chemical composition of the as-prepared products were characterized by using X-ray diffraction, transmission electron microscopy (TEM), high-resolution TEM, and energy dispersive X-ray spectroscopy. Results revealed that the as-synthesized CuInS2 colloid is in the tetragonal phase (size: 13-17 nm) and the AgInS2 in the orthorhombic structure (size: 17 +/- 0.5nm). A possible shape evolution and crystal growth mechanism has been suggested for the formation of pyramidal CuInS2 and rectangular AgInS2 colloids. Control experiments indicated that the morphology- and/or phase-change of CuInS2 and orthorhombic AgInS2 colloids are temperature- and/or time-dependent. CuInS2 colloids absorb well in the range of visible light at room-temperature, indicating its potential application as a solar absorber. Two photoluminescence (PL) subbands at 1.938 and 2.384 eV in the PL spectra of CulnS(2) colloids revealed that the recombination of the closest and the second closest donor-acceptor pairs within the CuInS2 lattice, in which the donor defect (Cu) occupies an interstitial position and the acceptor defect (V-In) resides at an adjacent cation site. In addition, the synthesis strategy developed in this study is convenient and inexpensive, and could also be used as a general process for the synthesis of other pure or doped ternary chalcogenides that require a controlled size (or shape). This process could be extended to the synthesis of other functional nanomaterials.

A Noninjection Reaction Route to CuInSe2Nanocrystals with Triethanolamine As the Complexing Agent

A Redox Reaction to Synthesize Nanocrystalline Cu2-xSe in Aqueous Solution

A Mild Solvothermal Route to Chalcopyrite Quaternary Semiconductor CuIn(SexS1 − X)2 Nanocrystallites

Colloidal synthesis of monodisperse quaternary CuInSSe nanocrystals

Preparation and Characterization of Cuins2 Thin Films for Solar Cells by Chemical Bath Deposition

Solvothermal Synthesis and Characterization of Chalcopyrite CuInSe2 Nanoparticles

Colloidal synthesis of zincblende Cu3InSnS5 nanocrystals and their application in the thin-film solar cell

Chemical synthesis of Cu(In) metal inks to prepare CuInS2 thin films and solar cells

Facile synthesis of CuSe nanoparticles and high-quality single-crystal two-dimensional hexagonal nanoplatelets with tunable near-infrared optical absorption

Cu–In Intermetallic Compound Inks for CuInS 2 Solar Cells

Synthesis and Characterization of CuZnSe2 Nanocrystals in Wurtzite, Zinc Blende and Core-Shell Polytypes

Cu2−xSe nanooctahedra: controllable synthesis and optoelectronic properties

Synthesis and Characterization of CIGS Powder

Shape- and Phase-Controlled Synthesis of Monodisperse, Single-Crystalline Ternary Chalcogenide Colloids Through A Convenient Solution Synthesis Strategy

Wurtzite CuIn(S x Se 1- x ) 2 Nanocrystals: Colloidal Synthesis and Band-Gap Engineering

Formation of High-Quality I-Iii-Vi Semiconductor Nanocrystals by Tuning Relative Reactivity of Cationic Precursors

Facile synthesis and characterization of CuInS2 nanocrystals with different structures and shapes

Phase-Selective Synthesis Of Cu2znsns4 Nanocrystals Through Cation Exchange For Photovoltaic Devices

Design of Chalcopyrite-Type CuFeSe2 Nanocrystals: Microstructure, Magnetism, Photoluminescence and Sensing Performances

A facile synthesis of a copper(I) thiourea sulphate complex and its application for highly efficient chalcopyrite solar cells

Colloidal Nanocrystals of Wurtzite-Type Cu2znsns4: Facile Noninjection Synthesis and Formation Mechanism