Effect of Tween 80 on Preparation of BiFeO3 in Microwave-Hydrothermal Method

郑玉芹,谈国强,博海洋,苗鸿雁,常美艳,夏傲

DOI: https://doi.org/10.14062/j.issn.0454-5648.2011.08.006

2011-01-01

Abstract:The pure phase of BiFeO3 powder was synthesized by a microwave-hydrothermal method with FeCl3·6H2O and Bi（NO3）3·5H2O powder as raw materials,KOH as mineralizer and Tween 80 as a surfactant.The effects of the amount of Tween 80 on morphology,phase composition and photocatalytic property of BiFeO3 powder were investigated.The results indicate that the single phase of BiFeO3 powder could be prepared via the microwave-hydrothermal method at 200 ℃ for 1 h with KOH of 1.5 mol/L,the volume fraction of Tween 80 of 0–1.7% and a mole ratio of Fe to Bi of 1.0.Morphology of the BiFeO3 powder became uniform hair ball-like when volume fraction of Tween 80 was less than 1.7%.When the hair ball-like BiFeO3 powder was used as a catalyst,deg-radation rate of Rhodamine B increased from 48.92% to 79.71% after 4 h UV light irradiation.The BiFeO3–Bi25FeO40 composite powder was prepared when volume fraction of the Tween 80 was higher than 1.7%.When the BiFeO3–Bi25FeO40 composite powder or the mixture of BiFeO3 and Bi25FeO40 powders were used as catalyst,degradation rates of Rhodamine B after 4 h UV light irradia-tion were 97.42% and 86.73%,respectively.When the BiFeO3 powder,the first reclaimation BiFeO3 powder or the second reclaima-tion BiFeO3 powder were used as catalyst,degradation rates of Rhodamine B after 4 h UV light irradiation were 79.71%,76.78% and 68.84%,respectively.