Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Formation Process Of Silver Nanoparticles In Dtab/Sdbs/Pvp Aqueous Solution

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Study on the Preparation of Spherical Nanosilver Particles Using Ammonium Citrate and Polyvinyl Alcohol as Surfactants

Preparation and Characterization of Silver Coated Hollow SnO2 Sphere with Open Structure

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

A Facile Synthetic Route to Aqueous Dispersions of Silver Nanoparticles

Silver Nanoparticles Capped by Oleylamine: Formation, Growth, and Self-Organization.

Preparation and Characterization of Silver Powders with Spheric Shape and Different Sizes

Nanocrystalline Silver Particles: Synthesis, Agglomeration, and Sputtering Induced by Electron Beam.

Large-scale synthesis and self-organization of silver nanoparticles with Tween 80 as a reductant and stabilizer

Preparation and Characterization of Stable Dispersive Colloidal Silver Nanoparticles

In-situ preparation of binary-phase silver nanoparticles at a high Ag+ concentration

Formation of Silver Nano Particles in Percolative Ag‐PbTiO 3 Composite Dielectric Thin Film

Metal-driven Viscoelastic Wormlike Micelle in Anionic/zwitterionic Surfactant Systems and Template-Directed Synthesis of Dendritic Silver Nanostructures.

Effects of Surfactants on Dispersive Performance of Ultrafine Silver Powder

Preparation of Nonaqueous Silver Nanosuspensions by in Situ Dispersion of the Surface-Modified Nanoparticles

Controlling the Growth and Assembly of Silver Nanoprisms

A mechanism study on the formation of silver nanorods

Synthesis of Silver Nanoparticles in Nonionic Surfactant System

Formation of CdS nanoparticles in mixed cationic-anionic surfactant vesicle system

Heterogeneous Nucleation and Growth of Silver Nanoparticles on Unmodified Polystyrene Spheres by in Situ Reduction