Abstract:A novel in situ autoreduction route has been developed, by which monodispersed silver nanoparticles with tunable sizes could be easily fabricated on silica-based materials, especially inside the channels of mesoporous silica (MPS). 13C CP/MAS NMR spectroscopy was employed to monitor the whole assembly process. It was demonstrated that the amino groups of APTS (aminopropyltriethoxyl silane)-modified MPS can be used to anchor formaldehyde to form novel reducing species (NHCH2OH), on which Ag(NH3)2NO3 could be in situ reduced. Monodispersed silver nanoparticles were thus obtained. In situ XRD and in situ TEM experiments were used to investigate and compare the thermal stabilities of silver nanoparticles on the external surface of silica gels (unconfined) and those located inside the channels of SBA-15 (confined). It was observed that unconfined silver nanoparticles tended to agglomerate at low temperatures (i.e., lower than 773 K). The aggregation of silver nanoparticles became more serious at 773 K. However, for those confined silver nanoparticles, no coarsening process was observed at 773 K, much higher than its Tammann temperature (i.e., 617 K). Only when the treating temperature was higher than 873 K could the agglomeration of those confined silver nanoparticles happen with time-varying via the Ostwald ripening process. The confinement of mesopores played a key role in improving the thermal stabilities of silver nanoparticles (stable up to 773 K without any observable coarsening), which is essential to the further investigations on their chemical (e.g., catalytic) properties.

Heterogeneous Nucleation and Growth of Silver Nanoparticles on Unmodified Polystyrene Spheres by in Situ Reduction

Investigation of heterogeneous nucleation-and-growth of silver nanoparticles on polystyrene spheres

A Facile Method to Synthesize PS/Ag Composite Micro-spheres

Time-Resolved Small-Angle X-ray Scattering Study on the Growth Behavior of Silver Nanoparticles

Preparation and Characterization of Silver Coated Hollow SnO2 Sphere with Open Structure

In-situ Formation of Silver Nanoparticles Stabilized by Amphiphilic Star-Shaped Copolymer and Their Catalytic Application

Toward Monodispersed Silver Nanoparticles with Unusual Thermal Stability.

Nanoporous Carbon Spheres and Their Application in Dispersing Silver Nanoparticles

Silver Nanoparticle Generators: Silicon Dioxide Microspheres.

Growth of Ag3Sn and Sn Nanoparticles Based on the Variation of Reaction Conditions

Controllable fabrication of PS/Ag core-shellshaped nanostructures

Synthesis of Ag-coated polystyrene colloids by an improved surface seeding and shell growth technique

Facile Synthesis of Monodisperse Silver Nanospheres in Aqueous Solution via Seed-Mediated Growth coupled with Oxidative Etching.

Controllable Growth of Silver-Seeded PbS Nanostructures

Facile Preparation of Silver Nanoparticles Homogeneously Immobilized in Hierarchically Monolithic Silica Using Ethylene Glycol As Reductant

Synthesis of Silver Nanoparticle-Coated Poly(styrene-Co-sulfonic Acid) Hybrid Materials and Their Application in Surface-Enhanced Raman Scattering (SERS) Tags

Nanospheres of Silver Nanoparticles: Agglomeration, Surface Morphology Control and Application As SERS Substrates

Synthesis of Monodisperse, Quasi-Spherical Silver Nanoparticles with Sizes Defined by the Nature of Silver Precursors.

Understanding And Controlled Growth Of Silver Nanoparticles Using Oxidized N-Methyl-Pyrrolidone As A Reducing Agent

Preparation of Polystyrene-Encapsulated Silver Hollow Spheres Via Self-Assembly of Latex Particles at the Emulsion Droplet Interface

Preparation of Nonaqueous Silver Nanosuspensions by in Situ Dispersion of the Surface-Modified Nanoparticles