Abstract:Gelcasting is a new ceramic forming technology for making complex-shaped ceramic products with high performance. The processes used in gelcasting are similar to processes often used in conventional ceramic forming process. However, when new high performance materials are introduced with the aim to improve the strength, defects such as air bubbles or agglomerates that can be found in many traditional ceramic materials are no longer be allowed since this would reduce the performance and reliability of the final ceramic products. The aim of this thesis project was to find an appropriate recipe of the ceramic suspension meanwhile improving the process of gelcasting and obtaining ceramic products with excellent mechanical behavior. To achieve this specified target, alumina and zirconia powders were studied in the following experiments which included rheological measurement of viscosity and storage modulus measurement for ceramic suspensions and drying shrinkage measurement of cast materials. The binder was burned out and the density was measured for ceramic materials sintered at different temperatures. The mechanical strength of sintered materials with high density was evaluated and the microstructure of fracture surfaces of ceramic samples was studied. Through rheological measurement, a good balance between fluidity and solid content of ceramic suspension was found. For alumina suspensions a solid content of 55vol% was selected and for zirconia solid contents of 46, 48 and 50vol% were studied. A monomer was dissolved in the suspension and an initiator was added to facilitate the polymerization of the monomer when the temperature was increased to around 70oC. The failure analysis of the fractured bending bars showed that the defects that caused the failure were not air bubbles but agglomerates. As a result, in future research for ceramic gelcasting with the intention to improve the mechanical strength, the suggestion is to use an appropriate recipe for the ceramic suspension and focus on elimination of granules and agglomerates from the suspension

Gelcasting of alumina ceramics using an egg white protein binder system

Natural additives in protein coagulation casting process for improved microstructural controllability of cellular ceramics

Effects of epoxy resin on gelcasting process and mechanical properties of alumina ceramics

Gel Casting of High Strength Ceramics

Gelcasting of alumina suspension using gellan gum as gelling agent

Alumina casting based on gelation of gelatine

New gel-casting process for alumina ceramics based on gelation of alginate

Thermoresponsive Gelcasting: Improved Drying of Gelcast Bodies

Gelcasting of Alumina Ceramic Components in Nontoxic Na-alginate–CaIO3–PVP Systems

Gelcasting of Alumina Ceramics with Improved Green Strength

Porous Alumina Ceramic Prepared by HEMA-TBA Gelcasting System

Ceramics with Ultra‐Low Density Fabricated by Gelcasting: an Unconventional View

Room-temperature Gelcasting of Alumina with Tartaric Acid and Glutaraldehyde

Freeze gelcasting of aqueous alumina suspensions for porous ceramics

Alumina gelcasting by using HEMA system

Gel-casting Without De-Airing Process Using Silica Sol As a Binder

Gelcasting of alumina ceramics in the mixed acrylamide and polyacrylamide systems

Ceramic in-situ forming based on gelation of sodium alginate

Research of (TBA)-Based Gel-Casting Process and (Water)-Based Foaming-Gel Process for Porous Alumina Ceramics Preparation

Fabrication of Alumina Green Body Through Gelcasting Process Using Alginate

Ceramic forming based on gelation principle and process of sodium alginate