Abstract:Lead zirconate titanate (PZT) ceramics were prepared by direct coagulation casting via high valence counterions (DCC–HVCI) using magnesium citrate as a coagulating agent assisted by the hydrolysis of glycerol diacetate. The colloidal behavior of PZT suspensions was evaluated by measuring the zeta potential and the viscosity. The dispersant content and solid loading were optimized to prepare concentrated PZT suspension. The results indicated that PZT suspension with solid loading up to 56vol% can be prepared by the addition of 0.5wt% ammonium polyacrylate at pH=10.6. The critical coagulation concentrations of magnesium and lead in 56vol% PZT suspensions are 15 and 35mM, respectively. The viscosity of 56vol% PZT suspensions with 0.5–1.0wt% magnesium citrate and 2vol% glycerol diacetate is higher than 30Pas at 60°C for 30min which is sufficient to coagulate the suspensions. The coagulating time is 60–90min at 50–70°C. The compressive strength of the coagulated wet samples decreases with the increase of coagulating temperature, but increases with the increase of magnesium citrate content. The strength is in the range 1.5–2.8MPa which is sufficiently high for demolding and handling without deformation. Dense PZT ceramics sintered at 1250–1280°C show homogeneous microstructures with relative densities of 99.2–99.7% and good piezoelectric properties compared with a traditional die pressing method.

Mechanical Reinforcement and Piezoelectric Properties of Pzt Ceramics Embedded with Nano-Crystalline

A Novel Approach to Improving the Electromechanical Properties of PZT-based Piezoelectric Ceramics Via a Grain Coating Modification Strategy

Enhancing Electrical Properties of High-Curie Temperature Piezoelectric Ceramics BNT-PZT and Their Mechanism

Enhanced Mechanical Behaviour of Lead Zirconate Titanate Piezoelectric Composites Incorporating Zinc Oxide Nanowhiskers

Mechanical Reinforcement and Piezoelectric Properties of Nanocomposites Embedded with ZnO Nanowhiskers

Nanoscale Insight Of High Piezoelectricity In High-T-C Pmn-Ph-Pt Ceramics

Enhanced Piezoelectric and Mechanical Properties of Zno Whiskers and Sb2o3 Co-Modified Lead Zirconate Titanate Composites

Lead zirconate titanate ceramics with aligned crystallite grains

Significantly Toughened PZT-based Piezoelectric Ceramics Simultaneously Keeping Excellent Electrical Properties Via Incorporating Trace Amount of Yttria-Partially-stabilized Zirconia

Enhanced Piezoelectric Properties of PZT Ceramics Prepared by Direct Coagulation Casting Via High Valence Counterions (DCC–HVCI)

Influence of Dispersed Coarse Grains on Mechanical and Piezoelectric Properties in (bi1/2na1/2)tio3 Ceramics

Fabrication, Microstructure and Properties of Zinc Oxide Nanowhisker Reinforced Lead Zirconate Titanate Nanocomposites

Significantly improved piezoelectric performance of PZT-PMnN ceramics prepared by spark plasma sintering

Grain size effect on piezoelectric properties of rhombohedral lead zirconate titanate ceramics

Piezoelectric and Mechanical Properties of CaO Reinforced Porous PZT Ceramics with One-Dimensional Pore Channels

Investigation of phase structure and electrical properties of PMN-PSN-PNN–PZT ceramics with different PNN content

Effect of Sintering Temperature and Time on Densification, Microstructure and Properties of the Pzt/Zno Nanowhisker Piezoelectric Composites

Effects of Sintering Behavior on Piezoelectric Properties of Porous Pzt Ceramics

Fabrication of Low Firing Piezoelectric Ceramics and Their Applications

PZT Based Piezoelectric Ceramics with Enhanced Fracture Toughness

PZT-based piezoelectric ceramics with complex structures