Abstract:The Laves phase alloy Tb-Dy-Fe, commercially known as Terfenol-D, exhibits the giant room-temperature magnetostriction at moderate field strength of a few kOe due to its combination of high magnetostriction and low magnetocrystalline anisotropic energy. Thus, this pseudobinary rare earth iron compound has found quite a number of applications such as in magnetomechanical transducers, actuators and adaptive vibration control systems. The simultaneous measurements of magnetostriction and magnetization at various fixed compressive pre-stresses applied in the axial direction for Tb 0.3 Dy 0.7 Fe 1.95 samples are presented. The results show that the magnetostriction increases with increasing compressive stress until it reaches 1742 × 10 6 under 25 MPa, so does the coercive magnetic field. And the hysteresis loop area for magnetization and magnetostriction also increases with the increment of applied compressive stresses. But the maximum magnetic susceptibility χ (d M/ d H ) is obtained under zero stress field and the strain derivative d λ /d H increases to the highest amplitude of 0.039 × 10 −6 A −1 m at a stress level of 5 MPa. In the strain versus magnetization intensity curve, the initial flat stage mainly consisting of a 180° domain wall motion becomes shorter with increasing stress. It means more initial domains are driven to the transversal direction under the compressive stress before magnetization, which is consistent with the improvement of the magnetostriction.

Grain-< 111 >-Oriented Anisotropy In The Bonded Giant Magnetostrictive Material

Structural Origin For The Local Strong Anisotropy In Melt-Spun Fe-Ga-Tb: Tetragonal Nanoparticles

Effect of Magnetic Annealing on Magnetostrictive Performance of a 〈110〉 Oriented Crystal Tb0.3Dy0.7Fe1.95

Magnetostriction Of < 110 > Oriented Crystals In Tb0.36dy0.64(Fe1-Xcox)(2) (X=0-0.30) Alloys

Induced Additional Anisotropy Influences on Magnetostriction of Giant Magnetostrictive Materials

Magnetostriction of a (110) oriented Tb0.3Dy0.7Fe1.95 polycrystals annealed under a noncoaxial magnetic field

-orientation growth of Tb-Dy-Fe alloys induced by high magnetic fields during directional solidification

Homogeneity of magnetostriction of Tb-Dy-Fe-Co 110 oriented alloy rod

Effect of magnetic annealing on magnetostrictive performance of a 〈1 1 0〉 oriented crystal Tb0.3Dy0.7Fe1.95

HOMOGENEITY OF MAGNETOSTRICTION OF Tb-Dy-Fe-Co ORIENTED ALLOY ROD

Magnetostriction of Tb–Dy–Fe alloy with different crystal axes orientation

Structure and Magnetostriction of Grain-Oriented Dy_(0.6) Tb_(0.3) Pr_(0.1) (fe_(0.95) Mn_(0.05) )_x Alloys

Magnetomechanical Behaviors of Giant Magneto Strictive Materials

Magnetostriction of 〈110〉 Oriented Crystals in Tb0.36Dy0.64(Fe1−xCox)2 (x = 0–0.30) Alloys

Anisotropic Magnetostriction in a ⟨110⟩ Oriented Crystal Tb0.36Dy0.64(Fe0.85Co0.15)2 after Coaxial Field Annealing

Design and Large Magnetostriction of Tb0.34Dy0.56Pr0.1Fe1.9/epoxy Composite Containing Near-Spherical Single-Crystal Particles

A Kind of Wide Operating Temperature Range Giant Magnetostrictive Alloys

Preparation of Terfenol-D Spherical Single-Crystal Particles and Study of Magnetostrictive Properties of Its Composites at Low Fields

Differential Magnetostrictive Response in Magnetically Annealed Tb0.36Dy0.64(Fe0.85Co0.15)2 with ⟨110⟩ Crystal Orientation

Variations in the Crystal Lattice of Tb-Dy-Fe Magnetostrictive Materials: The Lattice Constant Disturbance

Giant magnetostriction in Tb-doped Fe83Ga17 melt-spun ribbons