Abstract:Since the period required for testing the atmospheric corrosion of steel is long, most studies have focused on the corrosion behavior in less than three years, making exploring long-term atmospheric corrosion particularly valuable. This study investigates the corrosion behaviors, corrosion models, and mechanical properties of Q235 welded steel pipes collapsing due to corrosion after 25-year service in an urban industrial atmospheric environment using SEM, XRD, electrochemical methods, 3-D noncontact surface profilometry, and static tensile testing. The typical morphologies of & alpha;-FeOOH, & gamma;-FeOOH, and Fe3O4 and the effect of the content of various corrosive materials on the corrosion rate of the steel pipes are identified and analyzed. Then, the influence of different corrosion degrees on the mechanical properties of the steel pipes is examined by considering the morphologies of the rust pits. The results show that the wetting-drying cycles affect the structures of the rust layers and their protective properties. The rust layers on the sheltered surface are thicker but less protective than those on the exposed surface. In the wet state, FeSO4 accelerates ion transfer, while Fe3O4 facilitates electron transfer. These processes collectively contribute to the corrosion of Q235 steel. Moreover, as the time-of-wetness of the rust layers on sheltered specimens increases, the corrosion rate of Q235 steel also accelerates. The corrosion model combines pitting and uniform corrosion and gradually changes from predominated by pitting to thickness as the corrosion degree increases. The corrosion morphology impacts the mechanical properties of the welded steel pipes, and the influences of the thickness loss and maximum rust pit depth on these properties are profound.

Corrosion Behaviors of Several Kinds of Arc Sprayed Metal Coatings in Simulated Acid Soil Solution

Corrosion behaviors of arc spraying single and double layer coatings in simulated Dagang soil solution

Electrochemical Corrosion Behavior of Arc Sprayed Zn and Zn15Al Coatings in Simulated Salina Soil and Neutral Meadow Soil Solutions

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Corrosion Behaviors of Metal End of PHC Pipe Pile in Simulated Soil Solutions

Electrochemical Corrosion Behaviors of Three Commonly Used Metal Ends of PHC Pipe Pile in Simulated Soil Solutions

Effect of Al Content on the Long-Term Corrosion Behavior of Arc-Sprayed ZnAl Alloy Coatings

Corrosion Behavior of Arc-Sprayed Pore-Sealed Zn and Al Coatings in Seawater Containing Sulfate-Reducing Bacteria (SRB)

Corrosion Behavior of Copper Bearing Steels and the Derived In-Situ Coating

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Corrosion Behavior of 16mnr Steel and Welded Joints in High-Temperature Naphthenic Acid

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Corrosion behavior of low carbon steels and other non-ferrous metals exposed to a real calcareous soil environment

Corrosion Properties of Steel Sheet with Zinc-Base Alloy Coatings

Friction and anti-corrosion characteristics of arc sprayed Al+Zn coatings on steel structures prepared in atmospheric environment

Corrosion behaviour of 316L stainless steel and anti-corrosion materials in a high acidified chloride solution

Corrosion Behavior of High-Pressure Cold-Sprayed Zn30Al Alloy Coating on Q235 Steel

Corrosion behavior and antifouling ability of Cu-Zn-Al/Zn-Al composite coating on Q235 steel

Corrosion Electrochemical Behavior of 20 Steel and 16Mn Steel in Simulated CO2 Flooding Environment

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution

Preparation, Wear Resistance, and Corrosion Performance of Arc-Sprayed Zn, Al, and Zn-Al Coatings on Carbon Steel Substrates