Preparation and tribological properties of C/C-SiC composites by warm compacted-reactive melt infiltration process

Han Tuan-hui,Xiao Peng,LI Zhuan

2010-01-01

Abstract:The C/C-SiC composites were prepared by a new method of warm compaction-reactive melt infiltration (WC-RMI) process with short carbon fibers, graphite powders, Si powders and resins as raw materials. The friction and wear behaviors of C/C-SiC composites at different braking speeds were investigated. And the studies on WC-RMI method in theory were carried out. The results show that the density of C/C-SiC composites is 1.78 g/cm3, residual Si content is 0.3%, the friction coefficients are 0.36-0.43 and the wear loss decreases to 0.6×10-2 cm3/MJ. And the wear loss declines sharply at first and then keeps stable as the speed increases. The bright and smooth friction film in the course of friction forms on the C/C-SiC composites, which can decrease the wear loss obviously.