Abstract:The synergistic effect of metallic Ti and Zr as co-dopants on the reversible hydrogen storage properties of NaAlH4 was investigated systematically. Metallic Ti and Zr powders were used directly and separately as dopants, as well as used as co-dopants together in the preparation of NaAlH4 by hydrogenation of ball-milled mixtures of NaH/Al. The hydriding/dehydriding properties of the composites were then investigated. It was found that the addition of Ti and Zr powders together as co-dopants on hydriding/dehydriding properties is superior to doping with Ti or Zr alone. The highest reversible hydrogen capacity of the hydride doped with Ti and Zr together as co-dopants is 4.34wt% at 160∘C. The hydriding rate increases with the hydriding pressure increasing from 7.5 to 11.5MPa. The dehydriding kinetics is improved with the dehydriding temperature increasing from 90 to 130∘C, and the dehydriding rate of the composite doped with Ti and Zr as co-dopants is 1.6 and 2.0 times that of the sample doped with Ti and Zr alone at 130∘C. Microstructure analysis reveals that the improvement of the hydriding/dehydriding properties of NaH/Al (NaAlH4) can be partially ascribed to the in situ interaction of active titanium-hydride and zirconium-hydrides formed in the ball-milling process and subsequently acted as the catalytic active sites on the surface of hydride matrix. The effect of lattice expansion on enthalpy change indicates that the further improved dehydriding property of the composite can also be attributed to a favorable thermodynamic modification of the bulk composite hydride co-doped with Ti–Zr powders. In a word, the synergistic effect on the improvement of hydriding/dehydriding properties by introducing the addition of Ti–Zr together as co-dopants can be ascribed to both the “superficial catalytic process” and the “favorable thermodynamic modification” of the composite.

Effect of praseodymium and neodymium hydride catalysts on hydrogen storage properties of NaH/Al composite

Dehydriding Properties of Ti Or/and Zr-doped Sodium Aluminum Hydride Prepared by Ball-Milling

Reversible Hydrogen Storage Properties and Favorable Co-Doping Mechanism of the Metallic Ti and Zr Co-Doped Sodium Aluminum Hydride

Influence of Ti-Zr Catalysts on Reversible Hydrogen Storage Characteristics of NaH/Al Composite

Influence of Lanthanon Hydride Catalysts on Hydrogen Storage Properties of Sodium Alanates

Synergistic Effect of LiBH4and LiAlH4Additives on Improved Hydrogen Storage Properties of Unexpected High Capacity Magnesium Hydride

Remarkable Hydrogen Absorption/desorption Behaviors and Mechanism of Sodium Alanates In-Situ Doped with Ti-based 2D MXene

Effect of Rare Earth Doping on the Hydrogen Storage Performance of Ti1.02Cr1.1Mn0.3Fe0.6 Alloy for Hybrid Hydrogen Storage Application

Investigation of Hydrogen Storage Properties on the Mg-La-Ni Alloy Compounded with C@Pr2O3 Composite Catalyst

Preparation and hydrogen storage characteristics of Ti-NaAlH4 complex hydride

Hydrogen Absorption/desorption Properties of Li–Al–N–H Composite

Investigation on reversible hydrogen storage properties of Li3AlH6/2LiNH2 composite

Significantly Improved Hydrogen Storage Properties of Naalh4 Catalyzed by Ce-Based Nanoparticles

Hydrogen Storage Performance Of Libh4+1/2mgh(2) Composites Improved By Ce-Based Additives

Hydrogen Storage Performance of 2lih + MgB 2 Doped with Hydrothermal-Synthesized ZrO 2 Nanorods

Influence of Temperature and Hydrogen Pressure on the Hydriding/dehydriding Behavior of Ti-doped Sodium Aluminum Hydride

On the Effect of Different Sources of Al on the Properties of LiBH4 Hydrogen Storage

Carbon composite support improving catalytic effect of NbC nanoparticles on the low-temperature hydrogen storage performance of MgH2

Enhanced Hydriding−Dehydriding Performance of CeAl2-Doped NaAlH4 and the Evolvement of Ce-Containing Species in the Cycling

NbCl 5 and CrCl 3 Catalysts Effect on Synthesis and Hydrogen Storage Performance of Mg–Ni–NiO Composites

Superior Catalytic Effects of Nb2o5, Tio2, and Cr2o3 Nanoparticles in Improving the Hydrogen Sorption Properties of Naalh4