Cerium hydride generated during ball milling and enhanced by graphene for tailoring hydrogen sorption properties of sodium alanate
Hao-Yuan Zheng,Zhi-Qiang Ding,Yan-Jun Xie,Jun-Feng Li,Cun-Ke Huang,Wei-Tong Cai,Hai-Zhen Liu,Jin Guo
DOI: https://doi.org/10.1016/j.ijhydene.2020.10.184
IF: 7.2
2021-01-01
International Journal of Hydrogen Energy
Abstract:<p>In this study, NaAlH<sub>4</sub>−based hydrogen storage materials with dopants were prepared by a two-steps in-situ ball milling method. The dopants adopted included Ce, few layer graphene (FLG), Ce + FLG, and CeH<sub>2.51</sub>. The hydrogen storage materials were studied by non-isothermal and isothermal hydrogen desorption measurements, X-ray diffractions analysis, cycling sorption tests, and morphology analysis. The hydrogen storage performance of the as-prepared NaAlH<sub>4</sub> with Ce addition is much better than that with CeH<sub>2.51</sub> addition. This is due to that the impact of Ce occurs from the body to the surface of the materials. The addition of FLG further enhances the impact of Ce on the hydrogen storage performance of the materials. The hydrogen storage capacity, hydrogen sorption kinetics, and cycle performance of NaAlH<sub>4</sub> with Ce + FLG additions are all better than NaAlH<sub>4</sub> materials with the addition of either Ce or FLG alone. The NaAlH<sub>4</sub> with Ce and FLG addition starts to release hydrogen at 85 °C and achieves a capacity of 5.06 wt% after heated to 200 °C. The capacity maintains at 4.91 wt% (94.7% of the theoretical value) for up to 8 cycles. At 110 °C, the material can release isothermally a hydrogen capacity of 2.8 wt% within 2 h. The activation energies for the two hydrogen desorption steps of NaAlH<sub>4</sub> with Ce and FLG addition are estimated to be 106.99 and 125.91 kJ mol<sup>−1</sup> H<sub>2</sub>, respectively. The related mechanisms were studied with first-principle and experimental methods.</p>
energy & fuels,electrochemistry,chemistry, physical