Abstract:To explore an innovative approach to prepare high-performance Mo-based refractory alloys, the rapid solidification mechanisms of undercooled Mo-40%Co hyperperitectic alloy were investigated by both electromagnetic levitation (EML) and drop tube (DT) techniques. During EML experiments, typical peritectic solidification still prevailed even at the maximum undercooling of 252 K (0.14 T-T). The dendrite growth velocity of primary sigma-Mo3Co2 compound varied with alloy undercooling by a power relation, which attained 24.3 mm s(-1). As the bulk undercooling increased, the conspicuous dendrite fragmentation of primary phase took place, resulting in its grain refinement and volume fraction reduction. Meanwhile, the second recalescence degree exhibited a decreasing tendency, which indicated that the peritectic reaction was remarkably suppressed in the undercooled state. Under free fall condition, two critical diameters were determined for tiny alloy droplets and the corresponding undercooling thresholds were calculated as 361 and 443 K, respectively. When the alloy droplet was larger than 707 mu m, the typical peritectic solidification proceeded and the final microstructure was composed of primary sigma-Mo3Co2 dendrites and interdendritic epsilon-Mo6Co7 peritectic phase. With the reduction of droplet diameter, the direct nucleation of peritectic phase was induced. In this case, the epsilon-Mo6Co7 intermetallic compound regions appeared preferentially at the periphery of alloy droplets, whereas the typical peritectic microstructure filled in the center area. Once the droplet diameter decreased to 93 mu m, the peritectic solidification characteristics disappeared completely and the metastable epsilon-Mo6Co7 single phase became the unique growth morphology.

Microstructure Characteristics of Nanometer Fe Coated Mo Powders Prepared by Liquid Precipitation-Thermal Reduction Method

Study on Magnetic Properties and Nanocoating Structure of Co-Fe-P Alloy Coatings Obtained by Electroless Deposition

Rapid Growth Kinetics and Microstructure Modulation of Intermetallic Compounds Within Containerlessly Solidifying Mo-Co Refractory Alloys

Microstructure and Magnetic Properties of FeCoZr(Mo)BGe Nanocrystalline Alloys

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

Effect of Microstructure Evolution on Micro/Nano‐Mechanical Property of Fe–Co–Ni Ternary Alloys Solidified under Microgravity Condition

Effect of Minor Mo Addition on Microstructure and Corrosion Resistance of High-Velocity Air Fuel-Sprayed Fe-Based Amorphous Coatings

Study on reduction of MoO2 powders with CO to produce Mo2C

Microstructure and magnetic properties of nanocrystalline Co-doped Sendust alloys prepared by melt spinning

Preparation and characterization of Mo-Cu nanocomposite powders by chemical liquid reduction process

Preparation of Fe-coated Si3N4 Composite Powder by Heterogeneous Precipitation-Thermal Reduction Process

Effect of Reducing Time on the Structure and Magnetc Properties of FeCo/Al2O3 Nanocomposite

Microstructure Characteristics of Fe-Al Intermetallic Compound Coating Synthesized by Light Beam Alloying

Preparation and Microstructure of Nanocrystalline Fe-Ni-Mo Alloy with Low Mo and High Fe Content

Microstructural Characterization of Cold-Sprayed Nanostructured FeAl Intermetallic Compound Coating and Its Ball-Milled Feedstock Powders

Microstructure of Fe2(MoO4)3/Si3N4 composite powders by reduction and hot pressing

Microstructure and magnetic properties of Co/Al2O3 nanocomposite powders

Characterization of microstructure of nanostructured Fe-Si coating deposited by cold spraying

Formation Mechanism of Microstructure of Fe_2(MoO_4)_3/Si_3N_4 Composite Powder by Hydrogen Reduction

Microstructure, wear and electrochemical behaviors of laser cladding Fe-based coatings with various molybdenum contents

Microstructure of nanostructured Fe40Ni38Mo4B18 alloy