Effects of V-N Microalloying on Microstructure and Property in the Welding Heat Affected Zone of Constructional Steel
Kaiyu Cui,Haifeng Yang,Shengjie Yao,Zhengrong Li,Guodong Wang,Hongyun Zhao,Xinchen Nan
DOI: https://doi.org/10.3390/met12030480
IF: 2.695
2022-01-01
Metals
Abstract:Shielded metal arc welding and welding thermal simulation experiment were carried out for constructional steel containing 0% V and 0.10% V, and the microstructure, precipitation feature, microhardness HV0.2, and -20 degrees C impact value in the welding heat affected zone (HAZ) were investigated. The results showed that in the coarse-grained heat affected zone (CGHAZ), V and N were completely dissolved in the matrix of steel containing 0.10% V to promote the growth of prior austenite grains, meanwhile the fraction of high angle grain boundaries (HAGBs) decreased, thereby leading to the mean -20 degrees C impact value decreases from 87 J to 18 J. In the grain refined heat affected zone (GRHAZ), V(C, N) precipitates experience re-dissolution and re-precipitation at grain boundaries, V-N microalloying changes the microstructure from lath bainite + granular bainite + small amount of polygonal ferrite to polygonal ferrite + pearlite + martensite, thereby leading to the mean microhardness decreases from 335 HV0.2 to 207 HV0.2, and the mean -20 degrees C impact value decreased from 117 J to 103 J. In the intercritical heat affected zone (ICHAZ), V(C, N) precipitates experience re-dissolution, re-precipitation, and growth, causing the formation of micro-sized V(C, N) precipitates, thereby leading to the mean -20 degrees C impact value decreases from 93 J to 62 J.