Research on the low temperature co-fired NiCuZn ferrite materials and multilayer chip inductor applications
SU Hua,ZHANG Huai-wu
DOI: https://doi.org/10.3969/j.issn.1001-2028.2008.06.025
2008-01-01
Abstract:The main technical revolutions of the electrical information technology are figured of from analog to digital technologies,from fixed frequency to alterative frequency,from plug devices to chip devices.The multilayer chip inductors(MLCI) and the low temperature co-fired ferrites(LTCF) are the key technologies to realize the revolution of the third part.In this dissertation,the investigations are focus on the theories,technics and applications of the LTCF and MLCI.The research mode that combined theoretical analysis,materials preparation and element application are adopted to develop high performance low temperature co-fired NiCuZn ferrite materials,which are very suitable to produce multilayer chip inductors.In the part of theoretical analysis,the key factors to decide magnetic properties of the low temperature co-fired NiCuZn ferrite were investigated firstly,which were very helpful to control and improve these magnetic properties during experiments.Then the fired kinetics of the ferrite were analyzed to give directions to densify the ferrite under low fired temperature.To design compositions of the NiCuZn ferrite by permeability requirement,the expressions to calculate permeability of the ferrite were deduced.Then the genetic algorithm was adopted to optimize compositions of the NiCuZn ferrite,which evidently improved efficiency and speed of new material development.In the part of experimental investigations,the mixed-oxide method was first adopted to produce the NiCuZn ferrite.The influences of compositions on the fired behaviors,microstructures and magnetic properties of the ferrite were investigated.It is confirmed that x(CuO)=10.2% are appropriate to give attention to both low temperature co-fired characteristics and good magnetic properties of the NiCuZn ferrite.Then the effects of calcining temperature,milling time,heating rate and additives on the densification behaviors and magnetic properties of the ferrite were studied.It is confirmed that the optimal calcining temperature is 800 ℃;the optimal milling time is 24 h;the optimal heating rate is ≤2.5 ℃/min.To obtain the NiCuZn ferrite with high permeability,the mass fractions of optimal additives are 1.5%Bi2O3+0.3%WO3;to give attention to both permeability and Q-factor,the mass fractions of optimal additives are 1.5%Bi2O3+0.3%WO3+0.2%Co2O3.Then the sol-gel method was adopted to produce the NiCuZn ferrite.XRD method was used to identify the spinel structure of the xerogel,sol-gel auto-combustion prepared powder and fired samples.It is confirmed that the sol-gel auto-combustion prepared powder possesses single phase of the NiCuZn ferrite,and the particle size is in nano-scale.Then the fired behaviors and magnetic properties of the samples prepared by sol-gel method and mixed-oxide method were compared to ensure the advantages and disadvantages of the two methods.Finally,the combining method was adopted to produce the NiCuZn ferrite.It is confirmed that nanocrystalline ferrite particles enhance densification of the samples obviously.This factor was attributed to the nanocrystalline particles,which spread around the micron-sized ferrite particles,increased contacting area and inter-diffusion of the particles.Due to the nanocrystalline ferrite particles have the same chemical composition as the NiCuZn ferrite,high performance NiCuZn ferrite with low fired temperature is obtained.In the part of MLCI application research,the HFSS software was adopted to design,emulate and optimize the multilayer chip inductor first.It is confirmed that for the 0603-type multilayer chip inductor,when the length of the long side is chosen as 1 200 μm,length of the short side is chosen as 500 μm,width of the line is chosen as 100 μm,distance between line to the up and down side of the inductor is chosen as 150 μm,a high performance inductor is obtained.Then the prepared NiCuZn ferrite was chosen to produce the multilayer chip inductors by adopting LTCC technical line of UESTC.It is confirmed that the produced inductance values are lower than the forecast,which is mainly due to debasement of the permeability.However,the relationship between inductance values and turns of the coils is coincident with the forecast.