Abstract:Magnesium borate whisker (Mg2B2O5 w) reinforced Mg matrix composite was fabricated by vacuum-gas pressure infiltration process. The Mg2B2O5 w preforms forming process was determined. The Mg2B2O5 whiskers were fabricated into a preform by wet forming method without any binder. The Vacuum-Gas Pressure Infiltration process and parameters are also developed. The micrographs revealed reasonably uniform distribution and random orientation of the whiskers in the as-cast Mg2B2O5 w/AZ91D composite and the composites were without pores defect. The phases were analyzed by XRD patterns for the as-received whiskers, the whiskers sintered at 1 000 degrees C for 3 h and the as-cast composite, respectively. Then, the microstructure evolution of the composite was investigated when the composite was heat-treated. Meanwhile, the relationships between microstructure and micro-hardness of the alloy heat-treated were also studied. The heat-treatment condition were solution at 415 degrees C for 8 and 24 h, respectively, aging treatment at 200 degrees C for 8, 12, 16, 20 and 24 h, respectively and solution at 415 degrees C for 8 or 24 h and subsequent aging treated for 8, 12, 16, 20, 24 h, respectively. The phases were analyzed by XRD patterns for the composites after different heat treated process. The results of XRD patterns were shown to be in good agreement with the microstructures evolution of the composites. The results showed that the micro-hardness of the solution treated composites is decreased due to resolution of eutectic phase, whereas the micro-hardness of the aged composites was increased gradually and the peak hardness is reached to 201 HV in the composite aged for 16 hours. Solution treatment at 415 degrees C for 24 h, the beta-Mg17, Al12 phase is dissolved in the alpha-Mg phase to form oversaturated solid-solution in the composite and then the diffusive beta phase precipitates after subsequent aging treatment at 200 degrees C for 8 h; hence the micro-hardness of the composite was increased 30%. However, as the aging time increased to 24 h, the hardness of the composite was reduced to 183 HV because the beta-Mg17 Al12 phase precipitate changed from continuous fine platelets to discontinuous coarse platelets. It was concluded that the process of solution at 415 degrees C for 24 h and subsequent aging treatment at 200 degrees C for 8 h was the best process for the composite.

Preparation and Performance of the Magnesium Matrix Composite Reinforced with Al2O3-SiO2 Short Fibers

Microstructures and Mechanical Properties of Engineered Short Fibre Reinforced Aluminium Matrix Composites

Microstructure and Mechanical Properties of Squeeze Casting Quasicrystal Reinforced AZ91D Magnesium Matrix Composites

Development of AZ91D Magnesium Alloy-Graphene Nanoplatelets Composites Using Thixomolding Process

Magnesium Matrix Nanocomposites Fabricated by Ultrasonic Assisted Casting

Graphene Nanoplatelets Reinforced Magnesium Matrix Composites Fabricated by Thixomolding

Preparation and properties of nano-sized SiC particles reinforced AZ91D magnesium matrix composites

Effect of Heat Treatment on Microstructure and Mechanical Properties of Squeeze Cast n SiCp/AZ91D Magnesium Matrix Composites

Micro-structural and tensile strength analyses on the magnesium matrix composites reinforced with coated carbon fiber

The behaviour of AZ91 magnesium-based alloy with Ni–Al 2 O 3 reinforcement

Microstructural characteristic and mechanical properties of the in-situ MgAl2O4 reinforced Al matrix composite based on Al-Mg-ZnO system

Investigation and characteristics of AZ91 magnesium metal matrix composite using the powder metallurgy process

Fabrication of (TiB2 − TiC)p/AZ91 magnesium matrix hybrid composite

Mechanical Properties of Al Matrix Composite Enhanced by In Situ Formed SiC, MgAl2O4, and MgO via Casting Process

Silicon Carbide Particle Enriched Magnesium Alloy (AZ91) Composite: Physical, Microstructural and Mechanical Studies

Preparation of Al2O3/AZ91D Mg Interpenetrating Composites Using Lost Foam Casting Combined with Layered Extrusion Forming

Effect of Ti6Al4V reinforcement particles on the mechanical, wear, and corrosion properties of AZ91D magnesium matrix composites

Spectroscopic Characterization and Properties of Mg2B2O5w/AZ91D Magnesium Composites

Influence of hybrid reinforcements on the mechanical properties and morphology of AZ91 magnesium alloy composites synthesized by ultrasonic-assisted stir casting

Hybrid Filler Actions on Functional Performance Evaluation of Magnesium Alloy (AZ61) Hybrid Nanocomposites

Microstructural, hardness, and wear properties of Mg 2 Si-reinforced Al matrix in-situ composites produced by low superheat casting