Abstract:Magnesium‐lithium (MgLi) alloys have been widely used in various engineering fields due to their ultra-light characteristics. The strengthening of MgLi alloys is one of the key factors determining its application and has received extensive attention. In this work, the as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY (x = 0, 0.5 and 1.0, wt%) alloys with a density of only 1.52 g/cm3 were prepared via vacuum induction melting. The effects of rare earth element yttrium (Y) on the microstructure and mechanical properties of the MgLi alloy system were investigated. The results indicated that the microstructures of all the alloys mainly consisted of α-Mg, β-Li, AlLi, and MgLi2Al phases. The spherical AlLi phase was distributed inside the α-Mg and β-Li matrix. Part of the petal-like MgLi2Al phase was distributed in the interior of β-Li, and the rest grew along the grain boundaries as long strips. With the addition of Y, Al2Y phase formed with sharp edges and regular shapes. The Al2Y phase was mainly distributed inside the α-Mg phase and along the grain boundaries. Meanwhile, the amount of AlLi phase inside the α-Mg phase gradually decreased. The presence of nano-scale lath-shape MgLiZn phase in the β-Li matrix was observed in the HAADF map of the 0.5Y alloy. The continuous growth of MgLi2Al phase at the grain boundaries weakened its strength. As a consequence, it eventually led to intergranular fracture of the alloy. The 0.5Y alloy showed the highest tensile strength, up to ~244 MPa, and the yield strength was 60.5% higher than that of the 0Y alloy. Solid solution strengthening, precipitate strengthening and grain refinement were thus considered as the primary strengthening mechanisms caused by the addition of Y into the Mg-10Li-3Al-3Zn alloy.

Electrochemical formation of Mg-Li-Y alloys at solid magnesium electrode from LiCl-KCl-YCl3 melts

Electrochemical formation of Mg–Li alloys at solid magnesium electrode from LiCl–KCl melts

The Electrochemical Co-reduction of Mg-Al-Y Alloys in the LiCl-NaCl-MgCl 2 -AlF 3 -YCl 3 Melts

Electrochemical preparation and properties of a Mg–Li–Y alloy via co-reduction of Mg( ii ) and Y( iii ) in chloride melts

Electrochemical Codeposition of Mg–Li Alloys from a Molten KCl–LiCl–MgCl2 System

Study on the electrochemical behavior of Mg and Al ions in LiCl-KCl melt and preparation of Mg-Al alloy

Electrochemical Formation of Mg-Li-Ca Alloys by Codeposition of Mg, Li and Ca from LiCl-KCl-MgCl2-CaCl2 Melts.

Thermodynamic and Kinetic Properties of Mg(II) in LiCl-KCl Melt and the Formation of Zn-Mg Alloy on Liquid Zn Electrode

Electrodeposition of magnesium–lithium–dysprosium ternary alloys with controlled components from dysprosium oxide assisted by magnesium chloride in molten chlorides

The Cathodic Reduction of Magnesium in KCl-NaCl-MgCl2 Melts on a Platinum Electrode

Electrochemical Deposition of Al–Mg Alloys on Tungsten Wires from AlCl3–NaCl–KCl Melts

Electrochemical Behavior of Neodymium and Formation of Mg–Nd Alloys in Molten Chlorides

Improving the electrochemical behaviors and discharge performance of as-rolled Mg-4Li alloys through multicomponent alloying

Discharge performance of Mg-Y binary alloys as anodes for Mg-air batteries

Electrochemical removal of impurity mg from LiCl-KCl melts

Electrochemical Formation of Erbium-Aluminum Alloys from Erbia in the Chloride Melts

Electrodeposition of aluminum–magnesium alloys from an aluminum-containing solvate ionic liquid at room temperature

Electrochemical Corrosion Behavior of Mg-Al Alloy with Micro-Alloying of Yttrium in a Chloride Solution

Intercalation of Y in Mg-Al layered double hydroxide films on anodized AZ31 and Mg-Y alloys to influence corrosion protective performance

Electrochemical Extraction of Samarium from LiCl-KCl Melt by Forming Sm-Zn Alloys

Microstructure and mechanical properties of as-cast ultralight and high strength Mg-10Li-3Al-3Zn-xY alloy with multi-precipitates