Influence of microstructure and pH on corrosion behavior of Mg-Gd-Y-Zr magnesium alloy plate in acid rain

ZHANG Xin-ming,YI Jian-long,DENG Yun-lai,Jie Liu,TANG Chang-ping,Li Li
2010-01-01
Abstract:The corrosion behavior of Mg-Gd-Y-Zr T6 magnesium alloy plate in the stimulated acid rain was investigated by means of hydrogen evolution technology, polarization curve, electrochemical impedance spectroscopy, scanning electronic microscopy and X-ray diffractrometry. The shorter incubation period to the onset of corrosion, the more negative corrosion potential and the lower pH the higher corrosion rate value in stimulated acid rain is. The magnesium alloy plate prefers to local corrosion with high corrosion rate at initial stages. During corrosion incubation period, α-matrix dissolves preferentially while the second phase particles are left on the surface because they are inert to the corrosion attack. Corrosion rate slows down because the corrosion products pile up on the alloy plate surface. When the partially protective surface film is broken, corrosion rate of the plate is accelerated with a lot of pitting in the surface. The corrosion products contain magnesium hydroxide and magnesia. In the presence of carbon dioxide they are turned into Mg5 (CO3)4 (OH)2 · 5H2O.
What problem does this paper attempt to address?