Transitional dynamics of deformation induced phase transformation at ZrC/austenitic interface

Ming-hua TANG,Zhi-yi LIU,Shuang-kai HU,Xiao-ming JIN,Jian-zhong LI
2010-01-01
Abstract:The transitional dynamic relations of deformation induced ferrite transformation of low carbon manganese (niobium) steel containing ZrC particles under unidirectional compression thermal simulating condition were investigated. The results show that nucleation rate at austenite grain boundaries of the tested steel increases when ZrC particles are added, which affects deformation-induced ferrite morphology, distribution and its refinement. The increase of amount of the deformation induced ferrite is due to deformation enhancement in phase transformation. The decrease of size of deformation induced ferrite is due to the enhancement of recrystallization. And the deformation of the tested steel at low temperature in TAe3-TAr3 can accelerate ferrite nucleating. Meanwhile, as the deformation and recrystallization nucleus, ZrC particles with definite radius and suitable volume fraction (<0.6%), can hinder the movement of dislocation and can increase dislocation density, thus improve α-Fe nucleating rate, the critical volume fraction of ZrC particles is 0.6% which leads to the further refinement of ferrite grains of the tested steel at 900°C and strain rate of 1 s-1.
What problem does this paper attempt to address?