Abstract:Journal of Composite Materials, Ahead of Print. Using pre-stressed carbon fibre reinforced polymer/plastic (CFRP) to strengthen bridge structures is currently considered a promising technology and the durability of the structure is closely related to the material property. CFRP have good corrosion resistance, but they also experience different degrees of swelling, corrosion and hydrolysis in water immersion environments. Stress accelerates this effect and leads to deterioration of the mechanical properties of the materials. This work aims to investigate the durability of CFRP grids under water, wet-dry cycles of seawater, seawater immersion and 0% fu (fu is the ultimate tensile strength of the tested CFRP grids and it is constant stress in this paper), 30%fu, 60% fu coupled environments.Test aging time at room temperature (25°C) of 30, 60, 120, 180, 270, 360 days. The results indicate that the surface of epoxy resin is smooth at the initial moment by comparing of scanning electron microscope (SEM) image. With the increase of deterioration degree with aging time, the cavities and cracks appeared in the matrix. The epoxy resin content between the fibers decreased, and the adhesion force decreased. When the aging time is short, the tensile damage section of CFRP grid is flaky and the matrix is tightly bonded with the fiber. The later damage is mainly blow-up damage, which the fracture section is typical filiform. After CFRP grids aged for 360 days, the tensile strength decreased by 6.2%, 10.2%, 10.9% in the water, seawater solution and seawater wet-dry cycle environments. The tensile strength decreased by 10.2%, 12.3% and 20.2% under the coupling of seawater and different stress levels. A semi-empirical model of durability is proposed to provide a good reference value for the durability prediction of FRP materials.

Modeling and simulation of corrosion mechanism for glass fiber reinforced plastic in sea water

Modelling damage evolution of carbon fiber-reinforced epoxy polymer composites in seawater sea sand concrete environment

Hygrothermal aging effect on the water diffusion in glass fiber reinforced polymer (GFRP) composite: Experimental study and numerical simulation

A Corrosion Cracking Mechanism-Based Model with Molten Salt Corrosion Damage Coupling the Effect of Chloride Impurity and Plastic Deformation

Combined Effects of Sustained Loads and Wet-Dry Cycles on Durability of Glass Fiber Reinforced Polymer Composites

Effects of corrosion depths on flexural properties of glass fiber/unsaturated polyester composites in salt spray environment

Degradation of GFRP Bars with Epoxy and Vinyl Ester Matrices in a Marine Concrete Environment: an Experimental Study and Theoretical Modeling

Modeling of Load Responses and Aging of High Strength Fibers Considering UV-radiation

Influence of seawater sea sand concrete environment on the long‐term tensile properties of pultruded basalt and basalt‐carbon‐hybrid fiber reinforced polymer profiles

Analytical approach for crack identification of glass fiber reinforced polymer-sea sand concrete composite structures based on strain dissipations

Predicting Model of Composite Corrosion Life

Experimental investigation of long-term performance of fiber-reinforced epoxy and polyurethane polymer composites

Effect of sustained load and seawater and sea sand concrete environment on durability of basalt- and glass-fibre reinforced polymer (B/GFRP) bars

Accelerated Zero-Stress Hydrothermal Aging of Dry E-Glass Fibers and Service Life Prediction Using Arrhenius Model

Physicochemical-mechanical simulation of the short- and long-term performance of FRP reinforced concrete beams under marine environments

Tensile behavior and durability prediction of GFRP-steel composite bars under chloride environments

Effect of seawater and stress coupling on the durability of carbon fibre-reinforced polymer

Influence of Humidity on Fatigue Performance of CFRP: A Molecular Simulation

Experimental Study on the Mechanical Properties of CFRP/epoxy Composite Plates under Seawater Immersion

Molecular dynamics study on the effect of salt environment on interfacial structure, stress, and adhesion of carbon fiber/epoxy interface

Experimental Study of Micro-Cracks in Stress Corrosion of Fiber Reinforced Composites