Abstract:This paper reports a versatile and irreversible bonding method for poly(dimethylsiloxane) (PDMS) and SU-8. The method is based on epoxide opening and dehydration reactions between surface-modified PDMS and SU-8. A PDMS replica is first activated via the low-cost lab equipment, i.e., the oxygen plasma cleaner or the corona treater. Then both SU-8 and plasma-treated PDMS samples are functionalized using hydrolyzed (3-aminopropyl)triethoxysilane (APTES). Ultimately, the samples are simply brought into contact and heated to enable covalent bonding. The molecular coupling and chemical reactions behind the bonding occurring at the surfaces were characterized by water contact angle measurement and X-ray photoelectron spectroscopy (XPS) analysis. The reliability of bonded PDMS-SU-8 samples was examined by using tensile strength and leakage tests, which revealed a bonding strength of over 1.4 MPa. The presented bonding method was also applied to create a metal-SU-8-PDMS hybrid device, which integrated SU-8 microfluidic structures and microelectrodes. This hybrid system was used for the effective trapping of microparticles on-chip, and the selective releasing and identification of predefined trapped microparticles. The hybrid fabrication approach presented here, based on the PDMS-SU-8 bonding, enables multifunctional integration in complex microfluidic devices.

Soft Substrate As a Sacrificial Layer for Fabrication Free-Standing SU-8-based Nanofluidic System

Rapid Prototyping of Soft Lithography Masters for Microfluidic Devices Using Dry Film Photoresist in a Non-Cleanroom Setting

Free-standing SU-8 Gratings Fabricated by Sacrificial Layer-Assisted UV Curing Imprint

Fabrication of 1-d nanochannels on PMMA substrate by photoresist-free uv lithography and UV-assisted bonding under low temperature

Fabrication of Fluidic Chips with 1-D Nanochannels on PMMA Substrates by Photoresist-Free UV-lithography and UV-assisted Low-Temperature Bonding

Fabrication of Micro/nano Fluidic System Combining Hybrid Mask-Mould Lithography with Thermal Bonding

Fabrication of Size Controllable SU-8 Nanochannels Using Nanoimprint Lithography and Low-Pressure Thermal Bonding Methods

Fabrication of SU-8 Nanofluidic Channels by Reverse Thermal Bonding under Mild Conditions

Fabrication of a Three-Layer SU-8 Mould with Inverted T-shaped Cavities Based on a Sacrificial Photoresist Layer Technique

Fabrication of Enclosed Nanofluidic Channels by UV Cured Imprinting and Optimized Thermal Bonding of SU-8 Photoresist

Fabrication of micro/nano fluidic channels by nanoimprint lithography and bonding using SU-8

A Simple Method For Fabrication Of Microstructures Using A Pdms Stamp

Fabrication of an SU-8 Based Microfluidic Reactor on a PEEK Substrate Sealed by a Flexible Semi-Solid Transfer (FST) Process

Fabrication of Su-8 Moulds on Glass Substrates by Using A Common Thin Negative Photoresist As an Adhesive Layer

Fabrication of Size-Controllable Nanofluidic Channels Using Angled Physical Vapor Deposition

Wet releasing and stripping SU-8 structures with a nanoscale sacrificial layer

A simple method for fabricating multi-layer PDMS structures for 3D microfluidic chips

Low-Cost Fabrication Strategies of Microfluidic Device on Glass Substrate

A novel fabrication method of embedded micro-channels by using SU-8 thick-film photoresists

A Low-Cost Method of Fabricating Hybrid Micro-Nano Fluidic Chip by Double-Layer PDMS Mold and UV–thermal Nanoimprinting

A Versatile Bonding Method for PDMS and SU-8 and Its Application Towards a Multifunctional Microfluidic Device