Hydrothermal Preparation of Iron-Based Orthosilicate Cathode Materials with Different SiO2 Particles and Their Electrochemical Properties
Dichang Xiao,Lianyi Shao,Rui Ma,Miao Shui,Jiqing Gao,Fengtao Huang,Kaiqiang Wu,Shangshu Qian,Dongjie Wang,Nengbing Long,Yuanlong Ren,Jie Shu
DOI: https://doi.org/10.1016/s1452-3981(23)12828-8
IF: 1.541
2013-01-01
International Journal of Electrochemical Science
Abstract:Li2FeSiO4 and its derivates Li2Fe1-xMnxSiO4 (x = 0.0, 0.2, 0.4, 0.6 and 0.8) are prepared by a simple hydrothermal reaction using FeCl2•4H2O, MnCl2•4H2O, LiOH•H2O and SiO2 as starting materials. During the sample preparation, the crystallite size of Li2FeSiO4 is controlled by the particle size of SiO2 precursor. The as-prepared samples can be identified as orthorhombic phase with the space group of Pmn21, consisting of LiO4 and FeO4 tetrahedras linked to silicate [SiO4] 4oxo-anions in distorted hexagonal packing of oxygen ions with half of tetrahedral sites taken by Li, Fe, and Si. Electrochemical results show that Li2FeSiO4 prepared with smaller SiO2 particles shows higher reversible capacity and better cycle calendar life. The initial charge capacity and discharge capacity for Li2FeSiO4 prepared by 15 nm SiO2 particles are 126.4 and 123.4 mAh/g, respectively. By replacement of Fe by Mn in the structure of Li2FeSiO4, a series of orthorhombic Li2Fe1-xMnxSiO4 samples with x = 0.2, 0.4, 0.6 and 0.8 are hydrothermally prepared with 5 nm SiO2 particles and compared with each other. As a result, Mn-doped Li2Fe1-xMnxSiO4 samples show different variations on reversible capacity, capacity retention and cycling performance. It can be found that Li2Fe1-xMnxSiO4 samples with low Mn doping content (x = 0.0 and 0.2) can improve the reversible lithium storage capacity and capacity retention ability of iron-based orthosilicates. Among all the compounds, Li2Fe0.8Mn0.2SiO4 can deliver the highest lithium storage capacity of 107.4 mAh/g with the corresponding capacity retention of 83.0 % after 20 cycles.