TEMPERATURE SENSITIVITY OF MECHANICAL PROPERTIES OF CEMENT ASPHALT MORTARS

孔祥明,刘永亮,阎培渝

DOI: https://doi.org/10.14062/j.issn.0454-5648.2010.04.019

2010-01-01

Abstract:The compressive mechanical properties of cement asphalt mortars (CAMs) with varied asphalt to cement ratio (A) under different temperatures were investigated to reveal the temperature sensitivity of their mechanical properties. Uniaxial compressive stress-strain curves of different CAMs were obtained by the Material Testing System under different testing temperatures ranging from -40 to 80 °C. The correlation between peak stress or elastic modulus and temperature was acquired. The test results indicate that, higher temperature and higher A generally leads to lower peak stress and elastic modulus. At decreased temperature, a tough-brittle transition could be observed especially for the CAMs with high A. In high A range, the variation of A leads to less variation both on modulus and strengths. The hypothetical quantitative expressions of temperature dependency of elastic modulus and peak stress are validated by the testing results. It is proved that the defined temperature-sensitive factor could successfully characterize the dependency of CAMs' mechanical properties on temperature. The both testing results and calculated temperature-sensitive factors reveal that the mechanical properties of those CAMs with higher A show higher temperature sensitivity. For a given CAM, the temperature-sensitive factor of peak stress is larger than that of elastic modulus.