Preparation of the Initial Solid–liquid Interface and Melt in Directional Solidification of Al–18at%Ni Peritectic Alloy

Yanqing Su,Dongmei Liu,Xinzhong Li,Liangshu Luo,Jingjie Guo,Hengzhi Fu

DOI: https://doi.org/10.1016/j.jcrysgro.2010.05.018

IF: 1.8

2010-01-01

Journal of Crystal Growth

Abstract:The preparation of the initial solid–liquid interface and melt is a critical step in directional solidification process. Experiments on Al–18at%Ni peritectic alloy consisting of melting followed by thermal stabilization ranging from 0 to 2h were carried out in a Bridgman-type furnace. In the directional melting process, due to the temperature gradient imposed on the rod, a mushy zone was created between the complete liquid zone and non-molten solid zone parallel to the temperature gradient. With the thermal stabilization time increase, the volume fraction of the liquid inclusions in the mushy zone decreased. After 2h of thermal stabilization, the initial solid–liquid interface was corrugated, and the Ni concentration in the complete liquid melt zone was uniform but below the original composition. A solute diffusion transport model in a temperature gradient was proposed to describe the concentration evolution both in the mushy zone and the complete liquid melt zone during thermal stabilization.