Abstract:Polyimide-block-poly(dimethyl siloxane) copolymer was synthesized by a two-step process, initiated by coupling anhydride terminated poly(amic acid), AT-PAA with amino terminated poly(dimethyl siloxane), (NH 2 ) 2 -PDMS to form poly(amic acid)-block-poly(dimethyl siloxane). The resulting copolymer is then thermally treated to produce polyimide-block-poly(dimethyl siloxane), PI-PDMS. Because of the high glass transition temperature, Tg of polyimide, it is usually cured at a high temperature of about 300°C for over 2.5 h. Copolymerization of polyimide with polysiloxane, reduces the imidization temperature while maintaining high thermomechanical properties. A series of instruments were used to monitor the progress of copolymerization. The time-based analysis of the product of copolymerization enables the optimization of the structure and properties of the copolymers. The chemical structure and composition of the copolymer were studied by Fourier Transform Infrared Spectroscopy, (FT-IR). The incorporation of PDMS blocks into the copolymer and the degree of imidization of the polyimide block increased with increasing reaction time. The change in the viscosity of the copolymerizing solution was monitored by simple shear viscometry conducted with the Brookfield Viscometer. The reported increase in solution viscosity with increasing copolymerization time is associated with increasing molecular weight of the copolymer. The intrinsic viscosity of the copolymer solution was measured as a function of copolymerization time and it was found that the intrinsic viscosity of the copolymer solution increased with increasing reaction time. The glass transition temperature (Tg) and the thermal stability of the copolymer were determined by differential scanning calorimetry, DSC and thermogravimetric analysis, and TGA, respectively. Between 25°C and 420°C, the copolymers synthesized in this study show two glass transition temperatures due to the polyimide, PI block at around 380°C and another peak associated with PDMS plasticized polyimide at about 290–300°C. The two Tg peaks observed in the DSC thermogram are believed to be indicative of the structure of a block copolymer. TGA analysis shows that the thermoxidative stability of the copolymers increased with increasing reaction time, due to the incorporation of increased amount of PDMS unit into the copolymer. The combination of increasing molecular weight of copolymer, higher degree of imidization of polyimide blocks and enhanced thermoxidative stability may translate into improved flame retardancy of copolymers. This suggested enhancement in flame retardancy in air atmosphere, is believed to be due the incorporated PDMS blocks, which can be converted into silica, SiO2, a recognized thermally stable material.

Modification of Polyimide Films by Copolymerization and Blending

Preparation and Dielectric Properties of Polyimide/silica Nanocomposite Films Prepared from Sol–gel and Blending Process

PREPARATION AND STUDY ON STRUCTURE OF THE POLYIMIDE/SILICA HYBRID AND NANOCOMPOSITE FILMS

Structure and Properties of Thermoplastic Polyimide Based on 4', 4'-(Oxybis (methylene)) Bis ([1.1'- Bipheny]3-Amine) Diamine

Synthesis and Characterization of Polyimide from Hydrogenated Pyromellitic Anhydride

Effect of Isomerism on Mechanical and Tribological Properties of Thermoplastic Polyimide Films

Clarifying the effect of moisture absorption and high-temperature thermal aging on structure and properties of polyimide film at molecular dynamic level

Blends of thermoplastic polyurethane and polyether–polyimide: preparation and properties

Novel Polyimide-block-poly(dimethyl siloxane) copolymers: Effect of time on the synthesis and thermal properties

Effect of Blending Modifications for Phenylethynyl-terminated Polyimides

Fabrication and Properties of Polyimide Copolymer Fibers Containing Pyrimidine and Amide Units

Preparation of High-Temperature Resistant Polyimide Fibers by Introducing the p -Phenylenediamine into Kapton-Type Polyimide

Molecular Design, Synthesis and Characterization of Intrinsically Black Polyimide Films with High Thermal Stability and Good Electrical Properties

Synthesis and Properties of Optically Transparent Fluoro-Containing Polyimide Films with Reduced Linear Coefficients of Thermal Expansion from Organo-Soluble Resins Derived from Aromatic Diamine with Benzanilide Units

Infrared-Analysis Of The Irradiation Effects In Aromatic Polyimide Films

Characterization and Thermal Degradation of Polyimide Derived from 5-Amino-2(p-aminophenyl) Benzoxazole Monomer with Pyromellitic Dianhydride

Synthesis and Properties Study of Fluorinated Copolymer Polyimide

Enhanced Mechanical and Thermal Properties of Polyimide Films Using Hydrophobic Fumed Silica Fillers

Polymerization, Structure and Thermal Properties of Odpa-Dmb Polyimide Films

Impact of Modification of Carbon Black on Morphology and Performance of Polyimide/carbon Black Hybrid Composites.

Molecular dynamics simulation and performance analysis of polyimide/aramid blends