Microstructure, electrical properties and processing dependence of CuO modified (Na0 52K0.48)NbO3 ceramics

Shi Su,Ruzhong Zuo,Yan Ran,WanLi Zhao,Xiaohui Wang,Longtu Li

2010-01-01

Ceramics - Silikaty

Abstract:The CuO modified (Na0.52K0.48)NbO3 (NKN) piezoelectric ceramics were prepared by a solid-state reaction method. On the one hand, CuO doping can improve the densification behavior and simultaneously promote the grain growth, however, has little effect on the Curie temperature. On the other hand, the mechanical quality factor Q(m) obviously increases, the dielectric loss tan delta decreases, and the piezoelectric constant (133 and the planar electromechanical coupling coefficient k(p) tend to drop. Moreover, an obvious effect comes from the sintering conditions. The 1 mol% CuO doped NKN ceramics sintered at 1090 degrees C for 3 h own the electrical properties: Q(m) = 1727, tan delta = 0.29%. d(33) = 74 pC/N, k(p) = 0.22 and a dielectric constant epsilon(r) = 410. All these effects of CuO doping are considered to result from the liquid phase and oxygen vacancies formed during sintering.