Abstract:CO 2 capture using alkali metal salt (AMS)-promoted MgO-based sorbents at intermediate temperatures (300 – 500 °C) has gained increased interest recently. The prospects of such materials for CO 2 capture were assessed in this work. We investigated the most reactive MgO-based sorbents that have been reported in the literature, i.e., MgO promoted with a combination of various AMS (incl. NaNO 3 , LiNO 3 , K 2 CO 3 and Na 2 CO 3 ), and examined how particle size (from powder to pelletized 500 μm particles) and reaction conditions (calcination/carbonation temperature, and partial pressure of CO 2 ) affect the cyclic CO 2 uptake using a thermogravimetric analyzer (TGA) at ambient pressure. The TGA results showed that the CO 2 uptake of the sorbents decreased significantly after pelletization, losing 74 % of its initial capacity. However, the CO 2 uptake capacity of the pelletized sorbents continued to increase over 100 cycles and reached a value (~ 0.46 g CO2 /g sorbent ) close to that of the powdery sample (~ 0.53 g CO2 /g sorbent ). Analysis via X-ray diffraction (XRD), inductively coupled plasma optical emission spectroscopy (ICP-OES), scanning electron microscope (SEM) and N 2 physisorption suggests that the increase in CO 2 uptake was related to a change of the nature of the alkali species within the molten phase that is reflected by their re-crystallization behavior when cooling them down to room temperature, and appeared to be affected by the CO 2 partial pressure present during carbonation. Finally, the CO 2 capture performance of the best-performing sorbents was evaluated in a packed bed reactor, in order to assess whether the most reactive sorbents are capable of removing a significant amount of CO 2 from a gas stream at ambient pressure. The CO 2 uptake of the sorbents in the packed bed experiments was very close to that in the TGA experiments; however, the CO 2 capture efficiency was less than 10 %, which currently appears too low for an industrial post-combustion CO 2 capture process to be viable. New material developments should not only focus on improving the rate of formation of MgCO 3 from MgO, but also assess whether CO 2 removal with such sorbents is actually feasible.

MgO/Al2O3 sorbent for CO2 capture

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Characteristics of MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

The KMgAl Sorbents for CO2 Capture from Coal-Fired Power Plant

Co2 Capture over K2co3/Mgo/Al2o3 Dry Sorbent in A Fluidized Bed

Na2co3/Mgo/Al2o3 Solid Sorbents for Low-Temperature Co2 Capture

Study of the Novel Kmgal Sorbents for Co2 Capture

Ultrafast and Stable CO 2 Capture Using Alkali Metal Salt-Promoted MgO-CaCO 3 Sorbents.

Assessment of the Effect of Process Conditions and Material Characteristics of Alkali Metal Salt Promoted MgO-Based Sorbents on Their CO2 Capture Performance

High Temperature Co2 Capture Using Calcium Oxide Sorbent in A Fixed-Bed Reactor

Al 2 O 3 and CeO 2 -promoted MgO sorbents for CO 2 capture at moderate temperatures

Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica as Binder for Low-Temperature CO 2 Capture

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica As Binder for Low-Temperature CO2 Capture

Synthesis and low-temperature CO2 capture properties of a novel Mg-Zr solid sorbent

Synthesis and CO2 capture properties of mesoporous MgAl(O) sorbent

Understanding the CO2 Sorption Mechanisms of the MgO‐doped Na‐based Sorbent at Low Temperatures

Bench scale study of CO2 adsorption performance of MgO in the presence of water vapor

High‐Temperature Capture of CO2 on Lithium‐Based Sorbents Prepared by a Water‐Based Sol‐Gel Technique