Abstract:A new potassium-based adsorbent for CO2 capture with Al aerogel used as support is proposed in this work. The adsorbents with different surface modifiers (tetraethyl orthosilicate (TEOS) and trimethyl chlorosilane (TMCS)) and different K2CO3 loadings (10%, 20%, 30% and 40%) were prepared by sol-gel and iso-volume impregnation processes with ambient pressure drying. The CO2 adsorption performance of the adsorbents were tested by a fixed-bed reactor, and their adsorption mechanisms were studied by scanning electron microscopy (SEM), Brunauer Emmett Teller (BET), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, and X-ray fluorescence spectrometry (XRF). Furthermore, the adsorption kinetics and the cycling performance were investigated. The results show that using TEOS to modify the wet gel can introduce SiO2 to increase the strength of the skeleton. On the basis of TEOS modification, TMCS can further modify –OH, thus effectively avoiding the destruction of aerogel structure during ambient drying and K2CO3 impregnation. In this work, the specific surface area and specific pore volume of Al aerogel modified by TEOS + TMCS are up to 635.32 cm2/g and 2.43 cm3/g, respectively. The aerogels without modification (Al-B), TEOS modification (Al/Si) and TEOS + TMCS modification (Al/Si-TMCS) showed the best CO2 adsorption performance at 20%, 30% and 30% K2CO3 loading, respectively. In particular, the CO2 adsorption capacity and K2CO3 utilization rate of Al/Si-TMCS-30K are as high as 2.36 mmol/g and 93.2% at 70 degrees Celsius (°C). Avrami’s fractional order kinetic model can well fit the CO2 adsorption process of potassium-based adsorbents. Al-B-20K has a higher apparent activation energy and a lower adsorption rate during the adsorption process. After 15 adsorption-regeneration cycles, Al/Si-TMCS-30K maintain a stable CO2 adsorption capacity and framework structure, while the microstructure of Al/Si-30K is destroyed, resulting in a decrease in its adsorption capacity by nearly 30%. This work provides key data for the application of Al aerogel in the field of potassium-based adsorbent for CO2 capture.

Study of the Novel Kmgal Sorbents for Co2 Capture

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Characteristics of MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Carbon dioxide capture by functionalized solid amine sorbents with simulated flue gas conditions.

Study on CO2 Capture Performance by Potassium-Promoted MgAl-Hydrotalcite Adsorbent

Fabrication Of A New Mgo/C Sorbent For Co2 Capture At Elevated Temperature

Self-Assembled Core-Shell Structure MgO@TiO2 as a K2CO3 Support with Superior Performance for Direct Air Capture CO2

Development of New Potassium Carbonate Sorbent for CO2 Capture under Real Flue Gas Conditions

Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

Developing a Novel CaO-Based Sorbent for Promoted CO2 Capture and Tar Reduction

Kilogram-scale production and pelletization of Al-promoted CaO-based sorbent for CO2 capture

Investigation on a Novel CaO–Y2O3 Sorbent for Efficient CO2 Mitigation

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica as Binder for Low-Temperature CO 2 Capture

CO2 Adsorption Performance of Na/K-Impregnated MgO

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica As Binder for Low-Temperature CO2 Capture

Synthesis, Pelleting, and Performance Evaluation of a Novel K-Promoted Γ-Alumina/mgal-layered Double Oxide Composite Adsorbent for Warm Gas H2/CO2 Separation

K2CO3-Impregnated Al/Si Aerogel Prepared by Ambient Pressure Drying for CO2 Capture: Synthesis, Characterization and Adsorption Characteristics.