Abstract:Excessive emission of anthropogenic CO2 has facilitated greenhouse effect since the industrialized and modernized society, causing serious problems to both environment and human society. To alleviate this, Al-promoted CaO-based solid sorbents were produced on kilogram scale per batch via a simple and facile co-precipitation technique, in which Al served as an inert support and achieved an improvement on CO2 sorption performance of the sorbents. Preparation conditions of the mass-produced sorbents were optimized, including Ca/Al molar ratio, precursor concentration of calcium, coprecipitating temperature and time, which acted as critical roles in co-precipitation process. A 6-kg sorbent powder with favorable CO2 capture performance has been synthesized successfully at one batch. In addition, pelletization of the kilogram-scale produced sorbent powder was also executed utilizing extrusion-spheronized granulation methods. And a typical binder material (pseudo-boehmite) with peptizing agent (nitric acid) was incorporated to ameliorate nano-porous structure and mechanical reliability of sorbent pellets. The sorbent pellets, fabricated using the kg-scale produced powder, displayed a final CO2 sorption capability of 5.4 mol-CO2/kg-ads and great anti-attrition resistance (0.14 wt%/h) after 30 adsorption/desorption cycles up to 40 h.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to prepare Al - promoted CaO - based sorbents with high CO2 adsorption performance and good mechanical stability under large - scale production conditions. Specifically, the paper focuses on the following aspects: 1. **Large - scale production technology**: The paper studies the large - scale production technology of preparing Al - promoted CaO - based sorbents by the co - precipitation method. This technology needs to achieve scale - up production from the laboratory scale to the industrial scale while maintaining the sorbent performance obtained at the laboratory scale. 2. **Optimization of preparation conditions**: In order to improve the CO2 adsorption performance and cyclic stability of the sorbent, the paper optimizes the key parameters in the preparation process, including the Ca/Al molar ratio, the concentration of the calcium precursor, the co - precipitation temperature and time. These parameters have an important impact on the microstructure and performance of the sorbent. 3. **Granulation technology**: The paper also explores the technology of granulating the large - scale - produced sorbent powder by the extrusion - spheronization method. Pseudo - boehmite is used as a binder and nitric acid as a dispersant to improve the porous structure and mechanical strength of the particles. 4. **Performance evaluation**: The paper evaluates in detail the performance of the prepared sorbent in multiple CO2 adsorption/desorption cycles, including the CO2 adsorption capacity and anti - abrasion performance. The cyclic stability and anti - abrasion rate of the sorbent are tested by thermogravimetric analysis (TGA) and a fluidized - bed reaction system. In summary, the main objective of this paper is to develop an efficient and economical large - scale production method to prepare Al - promoted CaO - based sorbents with excellent CO2 adsorption performance and mechanical stability to meet the needs of industrial applications.

Kilogram-scale production and pelletization of Al-promoted CaO-based sorbent for CO2 capture

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Characteristics of MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure

Developing a Novel CaO-Based Sorbent for Promoted CO2 Capture and Tar Reduction

Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

Strengthening performance of Al-stabilized, CaO-based CO 2 sorbent pellets by the combination of impregnated layer solution combustion and graphite-moulding

Hydrophobic interface-assisted casting of Al-supported, CaO-based sorbent pellets for high-temperature CO 2 capture

A green and scalable synthesis of highly stable Ca-based sorbents for CO2 capture

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica As Binder for Low-Temperature CO2 Capture

One-step fabricated Zr-supported, CaO-based pellets via graphite-moulding method for regenerable CO2 capture

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica as Binder for Low-Temperature CO 2 Capture

Synthesis and Performance of a Nano Synthetic Ca-based Sorbent for High Temperature CO_2 Capture

Core-shell structured CaO-based pellets with enhanced cyclic CO2 capture performance

High-Entropy Fluorite Oxide-Modified CaO-Based Sorbent Pellets for Enhanced High-Temperature CO2 Capture

Wet Mixing Combustion Synthesis of CaO-based Sorbents for High Temperature Cyclic CO2 Capture

Development of New Potassium Carbonate Sorbent for CO2 Capture under Real Flue Gas Conditions

Improved performance of modified CaO-Al2O3 based pellets for CO2 capture under realistic Ca-looping conditions

New insights into stabilizing mechanism of Ca9Al6O18 stabilizing Ca-based sorbents for CO2 cyclic capture under mild conditions