Impact of a Spun-Cast MoO x Layer on the Enhanced Moisture Stability and Performance-Limiting Behaviors of Perovskite Solar Cells
Unyamanee Rosungnern,Pisist Kumnorkaew,Navaphun Kayunkid,Narong Chanlek,Youyong Li,I-Ming Tang,Non Thongprong,Nopporn Rujisamphan,Thidarat Supasai
DOI: https://doi.org/10.1021/acsaem.0c02963
IF: 6.4
2021-02-22
ACS Applied Energy Materials
Abstract:Organic–inorganic perovskite solar cells (PSCs), which have good environmental durability, are of great interest for practical applications. In this work, we show that a solution-processed MoO<sub><i>x</i></sub> layer acts as a buffer layer against high moisture stress to suppress defects in the perovskite and as a hole transport layer. The inversion of the photoinduced charge migration behaviors, that is, the electron preferentially moving toward the surface when MoO<sub><i>x</i></sub> is directly deposited onto the perovskite, is found to cause a significant loss in device functionality. The deposition of MoO<sub><i>x</i></sub> onto spiro-OMeTAD results in a lower photocurrent density–voltage (<i>J</i>–<i>V</i>) hysteresis behavior, a greatly enhanced electrical conductivity, and a significantly stabilized power conversion efficiency (PCE) when compared with those of devices without the MoO<sub><i>x</i></sub> layer. More importantly, the PCEs of the MoO<sub><i>x</i></sub>-based devices are retained at over 85% of their initial value, while only 75% is retained for a reference cell. This work highlights the facial fabrication approach of the solution-based MoO<sub><i>x</i></sub> layer and provides experimental evidence of the photogenerated charge migration behaviors on the perovskite/MoO<sub><i>x</i></sub> interface. This information would be beneficial for the further design and development of PSC technology.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c02963?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c02963</a>.XRD data of MoO<sub><i>x</i></sub> with annealing treatment at 150 and 425 °C and perovskite after exposure to moisture for various periods; magnified XRD signals of fresh perovskite and MoO<sub><i>x</i></sub>/perovskite as a function of the grazing angle; top-view SEM images of the perovskite capped with MoO<sub><i>x</i></sub> at various MoO<sub><i>x</i></sub> concentrations and of 0.02 M MoO<sub><i>x</i></sub> prepared on the spiro/perovskite/SnO<sub>2</sub> sample; cross-sectional SEM image of the MoO<sub><i>x</i></sub>/perovskite layer and AFM film thickness of 0.02 M MoO<sub><i>x</i></sub> coated on the glass slide; determination of an optical band gap (<i>E</i><sub>g</sub>) and Urbach tail energy (<i>E</i><sub>u</sub>) of the perovskite deposited with MoO<sub><i>x</i></sub>; steady-state PL spectra of the spiro/perovskite sample having MoO<sub><i>x</i></sub> and SnO<sub>2</sub> with different MoO<sub><i>x</i></sub> concentrations; XPS spectra of Mo 3d and O 1s of 0.02 M MoO<sub><i>x</i></sub>/perovskite after exposure to 1 sun for different periods; device parameters: short-circuit current (<i>J</i><sub>sc</sub>), open-circuit potential (<i>V</i><sub>oc</sub>), and FF of the device with and without MoO<sub><i>x</i></sub> as a function of aging time; and <i>J</i>–<i>V</i> curves of the device consisting of Ag/spiro-OMeTAD/MoO<sub><i>x</i></sub>/perovskite/SnO<sub>2</sub>/FTO-coated glass (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c02963/suppl_file/ae0c02963_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels