Abstract:A series of cross-linked sulphonated poly(sulphide sulphone) (SPSSF) membranes have been prepared via a polyphosphoric-acid-catalysed condensation reaction at 180 degrees C for a period of time (1.5-5.0 h) and the resulting cross-linking bonds are the highly stable sulphonyl groups. The cross-linking density could be controlled by regulating the reaction time. Cross-linking caused significant enhancement in the mechanical properties and large reduction in both water uptake (WU) and methanol permeability. The SPSSF-60 membrane (the numeral 60 refers to the degree of sulphonation), e.g. had a tensile strength increased from 16 to 27 MPa (wet membranes) after cross-linking for 5 h, while the WU substantially decreased from 320 to 58 wt.-% and the methanol permeability decreased from 1.9 x 10(-6) to 2.7 x 10(-7) cm(2) s(-1) (30 degrees C). Single cell test on hydrogen/oxygen revealed that the cross-linked SPSSF-50 (1.5 h) membrane displayed higher open circuit voltage (OCV, 1.02 V), higher maximum output power density (1.32 W cm(-2)) and significantly slower OCV decay rate than the uncross-linked SPSSF-40 membrane under the same operating conditions despite their similar ion exchange capacities. The crosslinked SPSSF-60 (5.0 h) and SPSSF-50 (1.5 h) membranes showed significantly better fuel cell performance than Nafion 212.

Preparation and properties of crosslinked sulphonated poly(sulphide sulphone)membranes for fuel cell applications