Abstract:Mordenite and ZSM-5 seeds could grow on the surface of an asymmetric α-Al2O3 support using an identical organic-free aluminosilicate solution under the same hydrothermal conditions. It suggests that the phase of zeolite can be controlled by varying the type of seed. Continuous mordenite and ZSM-5 membranes were prepared by the secondary growth method using corresponding seeds under appropriate conditions. The water content in the secondary growth mixture strongly influenced the growth of zeolite crystals. ZSM-5 seeds grew at a smaller rate and showed a habit of thin hexagonal plate in a concentrated mixture, while the crystals with a habit of rectangular parallelepiped were formed from a diluted secondary growth mixture. ZSM-5 crystals had poor intergrowth in the former case, whereas the crystals were highly intergrown in the latter case. ZSM-5 crystals in either membrane have a random orientation. In contrast to ZSM-5 zeolite, the crystal orientation in the secondary grown mordenite membranes strongly depended on the water content in the secondary growth mixture. The crystals in the mordenite membrane developed in a diluted secondary growth mixture were oriented with the (150) face parallel to the support surface, whereas the crystals in the membrane grown in a concentrated mixture were oriented with the (002) face parallel to the support surface. These results suggest that the crystal orientation in mordenite membranes can be manipulated only by changing the water content in a secondary growth mixture. The formation of the preferred crystal orientation in the secondary grown mordenite membrane is discussed in terms of an “evolutionary selection” process.

Preparation of silicalite-1 zeolite membrane on porous α-Al2O3 tube by modified secondary growth method and its characterization

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

The control of phase and orientation in zeolite membranes by the secondary growth method

Preparation of Zeolite NaA Membranes on Macroporous Alumina Supports by Secondary Growth of Gel Layers

Preparation of Mordenite Composite Membranes with Seeding

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Preparation of Asymmetric Zeolite NaA Membrane Layers by Vapor Phase Transfer and Seeded Growth Method

SYNTHESIS AND CHARACTERIZATION OF A-TYPE ZEOLITE MEMBRANES ON ALUMINA PARTICLES SURFACE

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

ZSM-5 zeolite membranes prepared from a clear template-free solution

Ultrasonic-assisted Fabrication of High Flux T-type Zeolite Membranes on Alumina Hollow Fibers

Growth Mechanism of a Preferentially Oriented Mordenite Membrane

The influence of nanoseeds on the pervaporation performance of MFI-type zeolite membranes on hollow fibers

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Influences of adding organic intermediate layer on membrane formation and properties

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Rapid and Facile Synthesis of Nanosized Silicalite-1 Zeolites from Solid Silica in a Semisolid-like System Via a Two-Step Crystallization Method

Induction of Zeolite Membrane Formation by Implanting Zeolite Crystals into the Precursor of Ceramic Supports

Fabrication of Zeolite Naa Membranes on Hollow Fibers Using Nano-Sized Seeds Exfoliated from Mesoporous Zeolite Crystals