Abstract:In this work, the hydrogen desorption properties of the novel Mg-Al-H hydrogen storage composites prepared by ball-milling the as-received magnesium hydride (MgH2) and the as-prepared aluminum hydride (AlH3) with different molar ratios (1:1, 1:0.5, and 1:0.25) are investigated systematically. Nonisothermal desorption measurements show that more than 7.51 wt % of hydrogen is released from the Mg-Al-H composites when they are heated from room temperature to 500 degrees C. Thermal analysis by differential scanning calorimeter (DSC) and hydrogen desorption spectrum by mass spectrometer (MS-H-2) are used synchronously to study the desorption process of the Mg-Al-H. The onset hydrogen desorption temperature of MgH2 in the MgH2 + AlH3 composite is dramatically reduced from 320 degrees C for the pure MgH2 to below 252 degrees C. The DSC/MS-H-2 and the X-ray diffraction (XRD) analyses show that the desorption of MgH2 in the Mg-Al-H composite is composed of two steps with the reaction between MgH2 and Al forming Mg17Al12 as the first step and the self-decomposition of the residual MgH2 as the second step. Isothermal desorptions show that the desorption kinetics of the MgH2 in the Mg-Al-H composite is significantly improved. The apparent activation energy for the desorption of MgH2 in the MgH2 + 0.25AlH(3) is reduced to 144.6 kJ/mol, which contributes to the improvement in the desorption kinetics of MgH2. The Johnson-Mehl-Avrami (JMA) kinetic studies indicate that the desorption kinetic model of MgH2 in the Mg-Al-H composite is different from the pure MgH2. Concerning the reversibility, under the conditions of 300 degrees C and 5 MPa H-2, MgH2 in the Mg-Al-H composite is almost fully recovered after absorption for 5 h while it is partially recovered for the pure MgH2. Among the samples studied, the MgH2 + 0.25AlH(3) composite exhibits the highest reversible hydrogen storage capacity of 6.10 wt % (H/M).

Hydrogen storage properties of Mg-50 vol.%V7.4Zr7.4Ti7.4Ni composite prepared by spark plasma sintering

Enhanced Hydrogen Storage Properties of MgH2 by the Synergetic Catalysis of Zr0.4Ti0.6Co Nanosheets and Carbon Nanotubes

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Hydrogen Storage Properties of Mg-doped Ti 1.2 Fe Alloys Synthesized by Mechanical Alloying

Hydrogen desorption properties of the MgH2-AlH3 composites

Achieving superior hydrogen storage properties of MgH<sub>2</sub> by the effect of TiFe and carbon nanotubes

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

Superior Hydrogen Storage Properties of MgH2–10 Wt.% TiC Composite

Study on Hydrogen Storage Characteristics of Mg-Cu Alloys

Preparation and Hydrogen Storage Properties of Mg-20 Wt.% Mg<sub>2</sub>Ni<sub>0.8</sub>Cr<sub>0.2</sub> Composite with TiO<sub>2</sub> Nanoparticles

Improved Kinetics of Nanoparticle-Decorated Mg-Ti-Zr Nanocomposite for Hydrogen Storage at Moderate Temperatures

Enhanced Hydrogen Storage Properties of Mg–Ti–V Nanocomposite at Moderate Temperatures

Hydrogen Storage Properties of Mg100−xNix (x = 5, 11.3, 20, 25) Composites Prepared by Hydriding Combustion Synthesis Followed by Mechanical Milling (HCS + MM)

Improved Hydrogenation Properties of Mg-x(Ti0.9 Zr0.2 Mn1.5 Cr0.3) Composites

Composite structure and hydrogen storage properties in Mg-base alloys

Hydrogen Storage Properties of Mg–TM–La (TM = Ti, Fe, Ni) Ternary Composite Powders Prepared Through Arc Plasma Method

Hydrogen Storage Properties of Core-Shell Structured Mg@TM (TM = Co, V) Composites

Catalytic effect of (Ti0.85Zr0.15)1.05Mn1.2Cr0.6V0.1Cu0.1 on hydrogen storage properties of ultrafine magnesium particles

Remarkable Synergistic Effects of Mg2NiH4 and Transition Metal Carbides (tic, ZrC, WC) on Enhancing the Hydrogen Storage Properties of MgH2