Abstract:For the purpose of elevated temperature service and weight reduction in aerospace vehicle applications, a novel Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal was employed to join TiAl to Ni-based superalloy (GH536). The effects of brazing temperature on interfacial microstructure and chemical composition of the joints were analyzed. The representative joint microstructure from TiAl substrate to GH536 substrate was primarily composed of four characteristic layers in order: B2; Al3NiTi2; AlNi2Ti containing Cr-rich (Cr, Ni, Fe)ss (subscript ss represents solid solution), Ni-rich (Ni, Cr, Fe)ss and TiNi3; Cr-rich (Cr, Ni, Fe)ss containing AlNi2Ti, Ni-rich (Ni, Cr, Fe)ss and TiNi3. Layer IV has the majority of the brazing seam, while Layer II was the thinnest. And the thickness of Layer II was not affected by brazing temperature. With the increase in brazing temperature in the range of 1110–1170 °C, both the shear strength and the thickness of brazing seam firstly increased and then decreased. The joint performance was jointly controlled by the thickness of brazing seam, the amounts of microcracks and intermetallic compounds formed in brazing seam. The maximum shear strength of 183 MPa at room temperature was obtained together with a peak thickness when the joint was brazed at 1150 °C for 10 min and the shear fracture mainly occurred in the thinnest Layer II Al3NiTi2.<h3 class="a-plus-plus">Graphic abstract</h3>

Interface Structure and Strength Analysis of Brazed GH3044 Nickel-Based Alloy Joint

Effect of brazing temperature on the interfacial microstructure and mechanical properties of GH3039 joint brazed with electroless Ni–P filler metal

Microstructure and shear strength of γ-TiAl/GH536 joints brazed with Ti−Zr−Cu−Ni−Fe−Co−Mo filler alloy

Microstructure evolution and mechanical properties of TiAl/GH536 joints vacuum brazed with Ti–Zr–Cu–Ni filler metal

Microstructure, mechanical properties and fracture behavior of GH3535 alloy joints brazed with Au-18Ni filler metal

Evolution of Interfacial Microstructure and Mechanical Properties of Nb521/GH99 Brazed Joints Using Ti–35Ni Filler Alloy

Interfacial Microstructure and Mechanical Properties of GH99 Superalloy and Nb Brazed Joint Using Cu75Pt25 Filler

Performance of the GH4169 Joint Using a Novel Ni-Based Amorphous Brazing Filler Metal

Interfacial Microstructure and Properties of TiC Cermet and GH3128 Joint Brazed Using AgCuNiLi

Microstructural Evolution and Mechanical Properties of Ti2AlNb/GH99 Superalloy Brazed Joints Using TiZrCuNi Amorphous Filler Alloy

Interfacial structure and properties of reactive brazing joints of TiAl/Ni-based alloy

Microstructural evolution and mechanical properties of Ni-based superalloy joints brazed using a ternary Ni-W-B amorphous brazing filler metal

Microstructure and mechanical properties of the brazed region in the AlCoCrFeNi high-entropy alloy and FGH98 superalloy joint

Interfacial microstructure and properties of Ti53311S titanium alloy joints brazed using TiZrNiCu filler metal

Interface structure and shear strength of brazed joints of TiAl-based alloy to middle-carbon steel

Interfacial microstructure and properties of brazing joints of TiAl/Ni-based alloy

Microstructure and shear strength of reactive brazing joints of TiAl/Ni-based alloy

Microstructure and mechanical properties of TiAl/Ni-based superalloy joints vacuum brazed with Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal

Microstructure and properties of the TiAl/GH3030 dissimilar joints vacuum-brazed with a Ti-based amorphous filler metal

Vacuum brazing TiAl intermetallics to GH3030 alloy with a multi-component Ti-based filler metal

Interfacial features of TiAl alloy/316L stainless steel joint brazed with Zr−Cu−Ni−Al amorphous filler metal