Abstract:This paper presents a comprehensive investigation of the effects of cutting parameters on the surface integrity of milled γ-TiAl alloys. Surface topography, surface roughness, surface defects, plastic deformation, micro-hardness, chip morphology, and tool wear of the milled γ-TiAl alloys were analyzed. The results indicate that the feed rate had the greatest influence on the surface topography and surface roughness. The value of surface roughness increased with the increase in cutting depth and feed rate. However, with the increase in cutting speed, it initially increased and then decreased. The minimum surface roughness was found to be 0.066 μm. The thickness of the plastic deformation layer and the micro-hardness value increased with the increase in cutting depth and feed rate. Also, they initially increased and then decreased with the increase in cutting speed. The minimum thickness of the plastic deformation layer was 15 μm and the depth of the hardened layer on the processed surface varied between 55 and 70 μm. The chip morphology was closely related to the quality of the processed surface. When the cutting depth and feed rate decreased, the chip morphology was transformed from segmented to nearly smooth. When the cutting depth and feed rate reached a critical point, plastic processing of γ-TiAl was achieved. Compared to brittle deformation, a more favorable processed surface was obtained. Finally, the comparison tests of tool wear were carried out with dry and flood coolant cutting. When the cutting speed reached 120 m/min in dry cutting, the tool life was very poor, and the cutting distance was only 1 m. However, the tool life was generally good when cutting with low cutting speed under the following conditions: vc = 60 m/min, ap = 0.1 mm, and fz = 0.01 mm/tooth. Under these conditions, the cutting distance was 60 m in dry cutting with the tool wear of 0.2 mm and 120 m in flood coolant cutting with the tool wear of 0.1 mm. The tool life in flood coolant operation was better than that of dry operation. The tool life decreased to 30 m when cutting with high cutting speed or feed rate (ap = 0.25 mm or fz = 0.025 mm/tooth).

Surface Roughness in High-Speed Side Milling of Hardened Mold Steel

Surface Characteristics and Roughness Prediction of TC4 Titanium Alloy in High Speed Grinding

Three-dimensional numerical simulation for high speed milling of aerospace aluminum alloy

Research on 3D Numerical Simulation and Experiment of Cutting Temperature for High Speed Milling of Aerospace Aluminum Alloy

Simulation of High-Speed Milling Process of Aerospace Aluminum Alloy

Influence of Tool Geometrical Parameters on High Speed Cutting of Titanium Alloy Ti6Al4V

Optimization of Surface Quality and Power Consumption in Machining Hardened AISI 4340 Steel

Research on Surface Roughness of High Speed Milling GH4169 by Orthogonal Test Method

Precision Prediction of Surface Roughness in High Speed Peripheral Milling Ti6Al4V Alloy

The Surface Integrity in Machining Hardened Steel Skd11 for Die and Mold

High-Speed Milling of Hardened Mold Steel P20 with Minimum Quantity Lubrication

Comparison in surface integrity and fatigue performance for hardened steel ball-end milled with different milling speeds

Surface integrity optimization for ball-end hard milling of AISI D2 steel based on response surface methodology

High speed machining of moulds and dies for net shape manufacture

Surface Roughness and Topography Analysis in Precision Milling of 3J33 Maraging Steel

The Comparative Studies on the Surface Integrity in Milling and Grinding Hardened Steel SKD11

Measurement of roughness on hardened D-3 steel and wear of coated tool inserts

Enhancing Tool Performance in High-Speed End Milling of Ti-6Al-4V Alloy: The Role of AlCrN PVD Coatings and Resistance to Chipping Wear

Study of surface integrity of milled gamma titanium aluminide

Study on 3D topography of machined surface in high-speed hard cutting with PCBN tool

Process parameter optimization and surface integrity evolution in the high-speed grinding of TiAl intermetallics based on grey relational analysis method