Abstract:PTFE adheres poorly to other materials due to its low surface energy and chemical inertness,which leads to failure of PTFE in many industrial applications.To spread the applications,numerous methods for surface modification have been developed to activate the PTFE surface for improving its wettability and adhesion ability.This study focused on the surface modification of expanded poly(tetrafluoroethylene)(ePTFE)film by a two-step process based on low-pressure plasma treatment followed by acrylic acid(AAc)graft copolymerization.The influences of different plasma treatments and graft copolymerization conditions on the hydrophilicity of film surface were studied.The wettability of the ePTFE film surface was determined by water contact angle,and the surface elemental compositions and the type of functional groups on the surface of the treated ePTFE samples were evaluated by X-ray photoelectron spectroscopy(XPS).The results indicated that the contact angle of ePTFE film declined from 145° to 102° when it was only treated by plasma treatment.After AAc grafted copolymerization,the contact angle decreased further to a smaller value.And the wettability of the film was improved obviously and kept constant.The condition of plasma treatment was He,100 W,90 s.The condition of AAc graft copolymerization was 30%(vol.),70℃,3 h.XPS analysis showed that the element ratio of F/C declined from 1.960 to 0.853,while the element ratio of O/C rose from 0 to 0.147.The result indicated that plasma treatment could greatly change the surface chemistry as well as morphology of ePTFE films.The surface roughness increased with plasma treatment time.From XPS measurements,it could be seen that the polar hydrophilic groups had been successfully grafted onto the ePTFE surface.The inert fluorine elements were partly replaced by oxygen polar groups,which was the fundamental reason for the improvement of hydrophilicity of ePTFE film.

Influence of Remote Oxygen Plasma Sterilization on Surface Property of Substrate Material

Studies on the Affinity Membrane for Adsorption and Purification of Lysozyme(I) - Influence of Low-temperature Oxygen Plasma Treatment on Surface Structure and Adsorption Properties of the Affinity Membrane

A low power 50 Hz argon plasma for surface modification of polytetrafluoroethylene

Surface Modification of Poly(tetrafluoroethylene) Films Via Plasma Treatment and Graft Copolymerization of Acrylic Acid

Influence of Oxygen Plasma Treatment on Poly(Ether Sulphone) Films

Surface Modification of Polytetrafluoroethylene by Microwave Plasma Treatment of H2O/Ar Mixture at Low Pressure

Characterization of Surface Modifications in Oxygen Plasma-Treated Teflon AF1600

Etching Processes of Polytetrafluoroethylene Surfaces Exposed to He and He-O2 Atmospheric Post-discharges

Femtosecond laser texturing assisted cold plasma hydrophilization of polytetrafluoroethylene surface

Cytocompatibility of titanium and poly(etheretherketone) surfaces after O2 non-thermal plasma sterilization

Surface modification by air-plasma treatment and its effect on the tribological behavior of hybrid fabric-polyphenylene sulfide composites

Enhanced Wettability and Adhesive Property of PTFE through Surface Modification with Fluorinated Compounds

PLASMA TREATMENT OF POLYTETRAFLUOROETHYLENE Ⅲ.XPS CHARACTERIZATION OF THE TREATED SURFACE

The stability of radio-frequency plasma-treated polydimethylsiloxane surfaces

Effect of Extreme Ultraviolet (EUV) Radiation and EUV Induced, N2 and O2 Based Plasmas on a PEEK Surface’s Physico-Chemical Properties and MG63 Cell Adhesion

Surface Composition and Surface Energy of Teflon Treated by Metal Plasma Immersion Ion Implantation

Surface modification of low temperature plasma-pretreated ePTFE film by AAc graft copolymerization

Investigation of the Impact of Cold Plasma Treatment on the Wettability of Medical Grade Polyvinylchloride

The Effect of Sterilization Treatment on the Surface Characteristics and Biological Activity of Zirconia Implant

Oxygen Ion Beam and Plasma Induced Blood Compatibility of Polyetherurethane

PTFE surface etching in the post-discharge of a RF scanning plasma torch: evidence of ejected fluorinated species