Abstract:PTFE adheres poorly to other materials due to its low surface energy and chemical inertness,which leads to failure of PTFE in many industrial applications.To spread the applications,numerous methods for surface modification have been developed to activate the PTFE surface for improving its wettability and adhesion ability.This study focused on the surface modification of expanded poly(tetrafluoroethylene)(ePTFE)film by a two-step process based on low-pressure plasma treatment followed by acrylic acid(AAc)graft copolymerization.The influences of different plasma treatments and graft copolymerization conditions on the hydrophilicity of film surface were studied.The wettability of the ePTFE film surface was determined by water contact angle,and the surface elemental compositions and the type of functional groups on the surface of the treated ePTFE samples were evaluated by X-ray photoelectron spectroscopy(XPS).The results indicated that the contact angle of ePTFE film declined from 145° to 102° when it was only treated by plasma treatment.After AAc grafted copolymerization,the contact angle decreased further to a smaller value.And the wettability of the film was improved obviously and kept constant.The condition of plasma treatment was He,100 W,90 s.The condition of AAc graft copolymerization was 30%(vol.),70℃,3 h.XPS analysis showed that the element ratio of F/C declined from 1.960 to 0.853,while the element ratio of O/C rose from 0 to 0.147.The result indicated that plasma treatment could greatly change the surface chemistry as well as morphology of ePTFE films.The surface roughness increased with plasma treatment time.From XPS measurements,it could be seen that the polar hydrophilic groups had been successfully grafted onto the ePTFE surface.The inert fluorine elements were partly replaced by oxygen polar groups,which was the fundamental reason for the improvement of hydrophilicity of ePTFE film.

Surface Composition and Surface Energy of Teflon Treated by Metal Plasma Immersion Ion Implantation

Surface Modification of Poly(tetrafluoroethylene) Films Via Plasma Treatment and Graft Copolymerization of Acrylic Acid

Surface Modification of Polymeric Materials by Plasma Immersion Ion Implantation

Plasma Ion Implantation to Thin Polymer Foils

Surface Treatment Of Polyethylene Terephthalate Using Plasma Ion Implantation Based On Direct Coupling Of Rf And High-Voltage Pulse

Surface modification of polytetrafluoroethylene by nitrogen ion implantation

Plasma-implantation-based surface modification of metals with single-implantation mode

Characterization of Surface Modifications in Oxygen Plasma-Treated Teflon AF1600

Surface Modification of Polyhydroxyalkanoates by Ion Implantation. Characterization and Cytocompatibility Improvement

Radiation Damage and Wettability Change of Low Energy C+ Implanted Polytetrafluoroethylene

Research On Surface Modification Of Polytetrafluoroethylene Coupled With Argon Dielectric Barrier Discharge Plasma Jet Characteristics

Femtosecond laser texturing assisted cold plasma hydrophilization of polytetrafluoroethylene surface

Plasma implantation based surface modification of metals with single-implantation mode

Surface metallization of PTFE and PTFE composites by ion implantation for low-background electronic substrates in rare-event detection experiments

Surface modification of low temperature plasma-pretreated ePTFE film by AAc graft copolymerization

Study on Computer Emulation of PTFE’s Wearability Improvement by Al3+ Ion Implantation

Surface Modification of Poly(propylene Carbonate) by Oxygen Ion Implantation

Modification of fluoropolymers by means of electron beam irradiation

Surface modification of a biomedical polyethylene terephthalate (PET) by air plasma

Surface modification of metals using high-frequency low-voltage plasma immersion ion implantation

Surface Metallization and Ceramic Deposition on Thermoplastic-Polymer and Thermosetting-Polymer Composite Via Atmospheric Plasma Spraying