Abstract:Fogging on transparent substrate greatly impacts transmittance, causing inconvenience and potential hazards. Increasing surface roughness to enhance hydrophilicity often reduces transmittance. Here, by enhancing the Marangoni flow to inhibit the coffee-ring effect during SiO2 droplet drying, we propose for the first time to manufacture superhydrophilic and high-transmittance coatings with porous structures on various substrates, including glass and resin. This approach relies on a simple, potentially large-scale ultrasonic spray method to enhance the Marangoni flow of SiO2 dispersion with different particle sizes by adding multiple surfactants to reduce the surface tension of the dispersion. The water contact angle of the SiO2 film decreases to below 5 degrees within 0.5 s, imparting anti-fogging properties to the substrate. The film exhibits a transmittance of 93.1 % at 580 nm, surpassing the inherent 90.8 % transmittance of the bare glass. Notably, the film shows remarkable selfcleaning properties due to potent hydration from eco-friendly SiO2 nanoparticles and the porous structure. Owing to the hydrogen bonding between tightly packed small-sized SiO2 particles as well as between the particles and substrate, the surface morphology of the film on glass remains intact even after washing, and soaking. The porous SiO2 film, with a contact angle dropping to below 5 degrees within 0.5 s, maintains its superhydrophilicity even after being exposed to high temperatures, UV irradiation, and humidity conditions. The simple production process of the porous SiO2 films offers a promising method for preparing high-transmittance anti-fogging films with significant industrial potential.

Design and fabrication of multilayer SiO2/CeO2-TiO2/SiO2 coatings with uv absorption and high quality transparence properties

A novel trilayer antireflection coating using dip-coating technique

Improved visible transparency of SIO2/ZNO:AL /CEO2-TIO2/SIO2 multilayer films with high UV absorption and infrared reflection rate

A Triple-layer Glass-coating for Low Emissivity and Photocatalytic Activity

Optimization of the thickness of glass/TiO 2/Ag/Ti/TiO 2/SiON multilayer film

Optimization of the thickness of glass/TiO2/Ag/Ti/TiO2/SiON multilayer film

A bi-layer glass-coating for low-e property and photocatalytic activity

Multifunctional composite multilayer coatings on glass with self-cleaning, hydrophilicity and heat-insulating properties

Growth of Low-Emissivity Films by RF Magnetron Reactive Sputtering

Preparation of multilayer coated glass with low-E and thermal insulation properties

Design and preparation of SiO 2/TiO 2/SiO 2-TiO 2 antireflective coatings with excellent abrasion-resistance and transmittance via sol-gel process

Structure and mechanical properties of TiAlSiN/Si3N4 multilayer coatings

Enhanced Marangoni Flow to Fabricate Uniform and Porous SiO2 Films: Toward Superior High Transparency, Antifogging, and Self- Cleaning Properties

Design and Preparation of SiO2/TiO2/SiO2-TiO2 Antireflective Coatings with Excellent Abrasion-resistance and Transmittance Via Sol-Gel Process

Layer-by-Layer Fabrication of High-Performance Broadband Anti-reflection Coatings Comprising Oppositely Charged Nanosheets and Nanoparticles

Mg-Doped Sio2 Porous Coating with High Anti-Reflection in the Visible Spectrum

Preparation and Characterizations of Fe/Ce Oxidation Nano Glass Coatings

Design and Preparation of Durable Double-Layer Non-Quarter-wave Antireflective Coatings

Low-Temperature Preparation of SiO2/Nb2O5/TiO2–SiO2 Broadband Antireflective Coating for the Visible via Acid-Catalyzed Sol–Gel Method

Preparation of SiO2:TiO2 for High-Performance Double Layer Anti-Reflection Coating

Characterization of SiO2 and TiO2 films prepared using rf magnetron sputtering and their application to anti-reflection coating