Abstract:In order to reveal the correlation between the accelerated corrosion test of epoxy polysiloxane coating and the real sea environmental test, the real sea environmental test was carried out in the atmosphere and tidal range area of Zhairuoshan Island in the East China Sea, and the multi-factor coupling test I (Cycle of 7-day xenon lamp aging test + 7-day Wetting-drying test) and test II (Cycle of 7-day xenon lamp aging test + 3-day damp heat test + 4-day salt spray test) were designed with reference to the environment of the East China Sea. The correlation between indoor accelerated corrosion test and real sea environmental test was analyzed by using Grey Relation Analysis, Spearman's rank correlation coefficient and Acceleration factor conversion method. The results show that both the indoor accelerated corrosion test and the real sea environmental test have corrosive effects on the epoxy polysiloxane coating of concrete. In the indoor accelerated corrosion test, it was found that the Wetting-drying test caused the highest loss of light rate. In the real sea environmental test, the loss of light rate of the coating in the atmosphere is higher than that in the tidal area, and the color difference is slightly lower. When the loss of light rate is used as the criterion, the grey correlation coefficient between the multi-factor coupling test I and the tidal range test is 0.63, and the maximum acceleration factor during the test is 5.3, indicating a good correlation between the two tests. Through this study, an effective indoor accelerated corrosion test method with good correlation and acceleration characteristics to the loss of light rate of concrete epoxy polysiloxane coating in a real sea environment was obtained.

Similar design on accelerated test of artificial climate simulation

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Optimization of field test method on durability of coastal concrete structure

Comparison of Chloride Penetration into Surface-Treated Concrete in Artificial and Natural Environments

Study on the Correlation Between Indoor Accelerated Corrosion Testing of Concrete Epoxy Polysiloxane Coating and Real-Sea Environmental Testing in the East China Sea

A New Test Method to Simulate Chloride Penetration into Concrete in Tidal Zone

Study of accelerated ageing test methods of sealant applied in curtain wall

Chloride Penetration in Surface-Treated Concrete in Natural and Accelerated Environments

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Durability related environmental zonation and design methodology for marine RC structures

A NEW SIMILARITY EXPERIMENTAL METHOD OF CONCRETE STRUCTURAL DURABILITY

A multi-environmental time similarity theory of life prediction on coastal concrete structural durability

EXPERIMENTAL ENHANCEMENT STUDY ON DURABILITY OF CONCRETE IN WHARF PROJECT

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Concrete surface chloride ion concentration varying with seasons in marine environment

Durability of Structural Adhesive Exposed to Marine Environment

Co-effects of initial and exposure environments on chloride penetration

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

Effecting Coefficients for Concrete Structure Durability Design Index

Service life prediction of marine concrete structurs

Influence of Initial Curing Conditions and Exposure Environments on Chloride Migration in Concrete Using Electrochemical Method