Abstract:Chloride ion erosion is an important factor affecting the durability of marine engineering concrete. In particular, concrete structures in wave splash and tidal zones are subjected to dry and wet cycles and multidimensional diffusion of chloride ions. To investigate the intricate diffusion of chloride ions within concrete under these dynamic conditions, we devised a comprehensive experiment. This experiment encompasses multiple dimensions, involving dry and wet cycles, as well as static immersion. The experiment intends to reveal how chloride ions are distributed in the concrete and clarify the changes that occur in its microstructure. Based on Fick's second law, the multidimensional diffusion model of chloride ions in concrete under the dry and wet cycles and static immersion was established by comprehensively considering the effects of chloride ion exposure time, environment temperature, relative humidity, and the action of dry and wet cycles. The results show that, under the same conditions, the chloride content in concrete decreases with the increase in penetration depth but increases with the increase in the chloride diffusion dimension and exposure time. Dry and wet cycles and multidimensional diffusion of chloride ions increase the development of cracks and pores in the concrete structure and generate large quantities of C3A·CaCl2·10H2O, which will exacerbate the chloride ion transport rate and penetration depth of concrete. Under the same exposure time and penetration depth, the chloride ion content in concrete under two-dimensional (2D) and three-dimensional (3D) diffusion under dry and wet cycles was 1.09~4.08 times higher than that under one-dimensional (1D) diffusion. The correlation coefficients between the simulation results of the multidimensional transport model of chloride ions in concrete under multi-factor coupling and the experimental results were all greater than 0.95, and the model can be utilized to predict the distribution of chloride ion concentration in concrete.

A New Test Method to Simulate Chloride Penetration into Concrete in Tidal Zone

Chloride Penetration in Surface-Treated Concrete in Natural and Accelerated Environments

Comparison of Chloride Penetration into Surface-Treated Concrete in Artificial and Natural Environments

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Comparative Study On Testing Methods Of Chloride Ions Diffusion Coefficient In Concrete

Experimental Study On Permeability And Chloride Resistance Properties Of Concrete In Yu-Cheng Bridge

Distribution of Chloride Accumulation in Marine Tidal Zone along Altitude

MECHANISM AND MATHEMATIC MODELING OF CHLORIDE PERMEATION IN CONCRETE UNDER UNSATURATED STATE

Numerical Simulation of Chloride Penetration in Concrete in Rapid Chloride Migration Tests

Peak Value Distribution of Surface Chloride Concentration and Convection Depth of Concrete

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone

Investigation on the Transport Properties of Chlorides in Concrete II Numerical Simulation

Multidimensional Transport Experiment and Simulation of Chloride Ions in Concrete Subject to Simulated Dry and Wet Cycles in a Marine Environment

Optimization of field test method on durability of coastal concrete structure

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Experimental and Numerical Study on the Microstructure and Chloride Ion Transport Behavior of Concrete-to-concrete Interface

Seasonal Variation of Surface Chloride Ion Content and Chloride Diffusion Coefficient in A Concrete Dock

Numerical Prediction of Chloride Penetration in Concrete Exposed to a Marine Environment at Tide

EXPERIMENTAL STUDY ON THE CHLORIDE DIFFUSION OF CONCRETE BASED ON ITS PORE STRUCTURE